Abstract: Novel bioabsorbable, nasal spreader graft implant devices are disclosed. The devices are useful in rhinoplasty and nasal reconstruction surgical procedures, as well as other surgical procedures. The devices have biodegradable core plates and biodegradable spreader plates or tissue ingrowth plates. The plates may have tissue ingrowth properties.

Abstract: Novel bioabsorbable, nasal spreader graft implant devices are disclosed. The devices are useful in rhinoplasty and nasal reconstruction surgical procedures, as well as other surgical procedures. The devices have biodegradable core plates and biodegradable spreader plates or tissue ingrowth plates. The plates may have tissue ingrowth properties.

Abstract: Novel bioabsorbable, nasal spreader graft implant devices are disclosed. The devices are useful to rhinoplasty and nasal reconstruction surgical procedures, as well as other surgical procedures. The devices have biodegradable core plates and biodegradable spreader plates or tissue ingrowth plates. The plates may have tissue ingrowth properties.

Abstract: Novel bioabsorbable, nasal spreader graft implant devices are disclosed. The devices are useful in rhinoplasty and nasal reconstruction surgical procedures, as well as other surgical procedures. The devices have biodegradable core plates and biodegradable spreader plates or tissue ingrowth plates. The plates may have tissue ingrowth properties.

Abstract: Novel bioabsorbable, nasal spreader graft implant devices are disclosed. The devices are useful in rhinoplasty and nasal reconstruction surgical procedures, as well as other surgical procedures. The devices have biodegradable core plates and biodegradable spreader plates or tissue ingrowth plates. The plates may have tissue ingrowth properties.

Abstract: A bimodal bioabsorbable polymer composition. The composition includes a first amount of a bioabsorbable polymer polymerized so as to have a first molecular weight distribution; a second amount of said bioabsorbable polymer polymerized so as to have a second molecular weight distribution having a weight average molecular weight between about 10,000 to about 50,000 Daltons, the weight average molecular weight ratio of said first molecular weight distribution to said second molecular weight distribution is at least about two to one; wherein a substantially homogeneous blend of said first and second amounts of said bioabsorbable polymer is formed in a ratio of between about 50/50 to about 95/5 weight/weight percent. Also disclosed are a medical device, a method of making a medical device and a method of melt blowing a semi-crystalline polymer blend.

Abstract: Compositions and methods of using tissue engineered blood vessels to repair and regenerate blood vessels of patients with vascular disease are disclosed.

Abstract: A bimodal bioabsorbable polymer composition. The composition includes a first amount of a bioabsorbable polymer polymerized so as to have a first molecular weight distribution; a second amount of said bioabsorbable polymer polymerized so as to have a second molecular weight distribution having a weight average molecular weight between about 10,000 to about 50,000 Daltons, the weight average molecular weight ratio of said first molecular weight distribution to said second molecular weight distribution is at least about two to one; wherein a substantially homogeneous blend of said first and second amounts of said bioabsorbable polymer is formed in a ratio of between about 50/50 to about 95/5 weight/weight percent. Also disclosed are a medical device, a method of making a medical device and a method of melt blowing a semi-crystalline polymer blend.

Abstract: Copolymers exhibiting the following combinations of properties, including without limitation, ?-caprolactone in an amount ranging from about 12 to about 70 mole percent, glycolide in an amount ranging from about 30 to about 88 mole percent, crystallinity ranging from about 10 to about 50% as measured by WAXD or about 10 to about 50 J/g as measured by DSC, and an inherent viscosity ranging from about 0.5 to about 1.45 dL/g as measured in a 0.1 g/dl solution of HFIP at 25° C.; a method for melt blowing such copolymers and nonwoven constructs produced therefrom are described herein.

Abstract: Novel bioabsorbable, nasal spreader graft implant devices are disclosed. The devices are useful in rhinoplasty and nasal reconstruction surgical procedures, as well as other surgical procedures. The devices have biodegradable core plates and biodegradable spreader plates or tissue ingrowth plates. The plates may have tissue ingrowth properties.

Abstract: A bimodal bioabsorbable polymer composition. The composition includes a first amount of a bioabsorbable polymer polymerized so as to have a first molecular weight distribution; a second amount of said bioabsorbable polymer polymerized so as to have a second molecular weight distribution having a weight average molecular weight between about 10,000 to about 50,000 Daltons, the weight average molecular weight ratio of said first molecular weight distribution to said second molecular weight distribution is at least about two to one; wherein a substantially homogeneous blend of said first and second amounts of said bioabsorbable polymer is formed in a ratio of between about 50/50 to about 95/5 weight/weight percent. Also disclosed are a medical device, a method of making a medical device and a method of melt blowing a semi-crystalline polymer blend.

Abstract: Copolymers exhibiting the following combinations of properties, including without limitation, ?-caprolactone in an amount ranging from about 12 to about 70 mole percent, glycolide in an amount ranging from about 30 to about 88 mole percent, crystallinity ranging from about 10 to about 50% as measured by WAXD or about 10 to about 50 J/g as measured by DSC, and an inherent viscosity ranging from about 0.5 to about 1.45 dL/g as measured in a 0.1 g/dl solution of HFIP at 25° C.; a method for melt blowing such copolymers and nonwoven constructs produced therefrom are described herein.

Abstract: A bimodal bioabsorbable polymer composition. The composition includes a first amount of a bioabsorbable polymer polymerized so as to have a first molecular weight distribution; a second amount of said bioabsorbable polymer polymerized so as to have a second molecular weight distribution having a weight average molecular weight between about 10,000 to about 50,000 Daltons, the weight average molecular weight ratio of said first molecular weight distribution to said second molecular weight distribution is at least about two to one; wherein a substantially homogeneous blend of said first and second amounts of said bioabsorbable polymer is formed in a ratio of between about 50/50 to about 95/5 weight/weight percent. Also disclosed are a medical device, a method of making a medical device and a method of melt blowing a semi-crystalline polymer blend.

Abstract: A semi-crystalline, absorbable copolyester composition comprising the reaction product of a polycondensation polyester and at least one lactone, wherein the polycondensation polyester comprises the reaction product of diglycolic acid and/or a derivative thereof and diethylene glycol; and the copolyester comprises about 30 to 60% by weight of the polycondensation polyester based on the total weight of the copolyester. Also medical devices such as absorbable sutures comprising such copolyesters and absorbable microspheres comprising such copolyesters and methods of making of such absorbable microspheres. Additionally, a method of melt blowing an absorbable copolyester composition and a nonwoven construct are disclosed.