Abstract: A method of making a fuser member having a support comprising the steps of: A) providing a support; B) coating from an organic solvent onto the support a coating composition comprising a fluorocarbon thermoplastic random copolymer, a curing agent having a bisphenol residue, a particulate filler containing zinc oxide, an aminosiloxane, and antimony-doped tin oxide particles, the fluorocarbon thermoplastic random copolymer having subunits of: —(CH2CF2)x—, —(CF2CF(CF3)y—, and —(CF2CF2)z—, wherein x is from 1 to 50 or 60 to 80 mole percent, y is from 10 to 90 mole percent, z is from 10 to 90 mole percent, x+y+z equals 100 mole percent; and C) curing the coating composition for 5 to 10 hours at a temperature in the range of 25° C. to 275° C.

Abstract: A fuser member comprising a core and a layer overlying the core, the layer including a fluorocarbon random copolymer, a curing agent which cures the fluorocarbon random copolymer, the cured fluorocarbon random copolymer having subunits of: —(CH2CF2)x—, —(CF2CF(CF3))y—, or —(CF2CF2)z—, wherein x is from 30 to 90 mole percent, y is from 10 to 70 mole percent, z is from 0 to 34 mole percent; x+y+z equals 100 mole percent. The layer further including a particulate filler having aluminum oxide, having a total concentration in the layer of from 10 to 140 parts by weight per 100 parts of the fluorocarbon random copolymer, and alkaline earth metal oxides or alkaline earth metal hydroxides or combinations thereof; and siloxane polymer comprising one or more curable, silanol-terminated, polyfunctional poly(C1-6 alkyl)siloxane polymers.

Abstract: A fuser member comprising a support and a layer overlying the support, the layer including a fluorocarbon thermoplastic random copolymer, a curing agent having a bisphenol residue, a particulate filler containing zinc oxide, an aminosiloxane, the cured fluorocarbon thermoplastics random copolymer having subunits of: —(CH2CF2)x—, —(CF2CF(CF3)y—, and —(CF2CF2)z—, wherein: x is from 1 to 40 or 60 to 80 mole percent, z is greater than 40 to no more than 89 mole percent, and y is such that x+y+z equals 100 mole percent.

Abstract: A fuser member whose outermost layer comprises a fluorocarbon-silicone interpenetrating network, comprising: (a) a first polymer comprising a fluorocarbon elastomer; (b) a second polymer selected from a curable polyfunctional poly(C(1-6) alkyl)siloxane polymer; a curable polyfunctional poly(C(1-6) alkyl)arylsiloxane polymer; and combinations thereof; and (c) a functionalized polydimethylsiloxane containing amine groups.

Abstract: A fuser member comprising a core and a layer overlying the core, the layer including a fluorocarbon random copolymer, a curing agent which cures the fluorocarbon random copolymer, the cured fluorocarbon random copolymer having subunits of: —(CH2CF2)x—, —(CF2CF(CF3))y—, or —(CF2CF2)z—, wherein x is from 30 to 90 mole percent, y is from 10 to 70 mole percent, z is from 0 to 34 mole percent; x+y+z equals 100 mole percent. The layer further including particulate filler having zinc oxide and yellow iron oxide and siloxane polymer comprising one or more curable, silanol-terminated, polyfunctional poly(C1-6 alkyl)siloxane polymers.

Abstract: A photoreceptor cleaning brush for an electrostatographic imaging apparatus contains individual fibers provided with a finishing agent that is a water-miscible aliphatic organic compound containing a plurality of alcoholic hydroxy substituents. The finishing agent is selected from the group of compounds having a molecular weight of up to about 250 and polyethylene glycols having a number-average molecular weight of about 1000 to about 200,000. In an electrostatographic imaging apparatus, the photoconductive imaging element includes the described photoreceptor cleaning brush and a photoconductive surface portion that contains a polycarbonate binder resin. The cleaning brush removes toner from the photoconductive surface portion of the element without damaging it.

Abstract: A photoreceptor cleaning brush for use in an electrostatographic imaging apparatus comprises individual fibers provided with a finishing agent comprising a water-miscible aliphatic organic compound containing a plurality of alcoholic hydroxy substituents. The finishing agent is selected from the group of compounds having a molecular weight of up to about 250 and polyethylene glycols having a number-average molecular weight of about 1000 to about 200,000. An improved electrostatographic imaging apparatus includes a photoconductive imaging element and a photoreceptor cleaning brush. The improvement comprises: the photoconductive imaging element having a photoconductive surface portion comprising a polycarbonate binder resin, and the cleaning brush comprising individual fibers provided with a finishing agent comprising a water-miscible aliphatic organic compound containing a plurality of alcoholic hydroxy substituents.

Abstract: A fuser member having a support metallic core and a layer of material formed over the metallic core, the layer includes composite material, including a high molecular weight reactive polyfunctional poly(C(1-6) alkyl)siloxane polymer; a cross-linked poly(dialkylsiloxane) incorporating an oxide, wherein the poly(dialkylsiloxane) has a weight average molecular weight before crosslinking of about 5,000 to 80,000; and a silane crosslinking agent.

Abstract: A method of preparing a composition containing a fluorocarbon thermoplastic random copolymer comprising the steps of: (a) providing a mixture having: (i) a fluorocarbon thermoplastic random copolymer having subunits of: —(CH2CF2)x—, —(CF2CF(CF3)y—, and —(CF2CF2)z—,  wherein x is from 1 to 50 or 60 to 80 mole percent, y is from 10 to 90 mole percent. z is from 10 to 90 mole percent. x+y+z equals 100 mole percent; (ii) a filler comprising zinc oxide; (iii) a curable amino functional polydimethyl siloxaie copolymer comprising aminofunctional units selected from tile group consisting of (aminoethylaminopropyl) methyl, ( aminopropyl) methyl and (aminopropyl) dimethyl; and (iv) a bisphenol residue curing agent; and (b) curing the mixture for 3 to 10 hours at a temperature in the range of 220° C. to 280° C. and for an additional 2 to 10 hours at a temperature in the range of 250° C. to 270° C.

Abstract: A composition comprising a fluorocarbon thermoplastic random copolymer, a curing agent having a bisphenol residue, a particulate filler containing zinc oxide, and an aminosiloxane, the cured fluorocarbon thermoplastic random copolymer having subunits of: —(CH2CF2)x—,—(CF2CF(CF3)y—, and —(CF2CF2)z—, wherein x is from 1 to 50 or 60 to 80 mole percent, y is from 10 to 90 mole percent, z is from 10 to 90 mole percent, x+y+z equals 100 mole percent.

Abstract: A toner fuser roller with suppressed electrostatic charge build-up for fixing a toner image to a receiver comprising: (a) a core; and (b) an overcoat layer formed over the core and defining a surface that contacts the receiver, the overcoat layer including electrically conductive fine powder in an amount of 10 to 29 weight percent so as to make the overcoat layer electrically conductive and suppress electrostatic charge build-up and improve thermal conductivity.

Abstract: A method of preparing a composition containing a fluorocarbon thermoplastic random copolymer comprising the steps of: (A) providing a mixture having: (i) a fluorocarbon thermoplastic random copolymer having subunits of: —(CH2CF2)x—, —(CF2CF(CF3)y—, and —(CF2 CF2)z—,  wherein x is from 1 to 50 or 60 to 80 mole percent, y is from 10 to 90 mole percent, z is from 10 to 90 mole percent, x+y+z equals 100 mole percent; (ii) a filler comprising zinc oxide; (iii) a curable amino functional polydimethyl siloxane copolymer comprising aminofunctional units selected from the group consisting of (aminoethylaminopropyl) methyl, (aminopropyl) methyl and (aminopropyl) dimethyl; and (iv) antimony-doped tin oxide particles; (v) a bisphenol residue curing agent; and (B) curing the mixture for 5 to 10 hours at a temperature in the range of 25° C. to 275° C.

Abstract: A composition including a fluorocarbon thermoplastic random copolymer, a bisphenol residue curing agent, a particulate filler having zinc oxide, antimony-doped tin oxide particles and aminosiloxane, the cured fluorocarbon thermoplastics random copolymer having subunits of: —(CH2CF2)x—, —(CF2CF(CF3)y—, and —(CF2CF2)z—, wherein x is from 1 to 50 or 60 to 80 mole percent, y is from 10 to 90 mole percent, z is from 10 to 90 mole percent; and x+y+z equals 100 mole percent.

Abstract: A method of making a fuser member having a support comprising the steps of: a) providing a support; b) coating from an organic solvent onto said support a coating composition comprising a fluorocarbon thermoplastic random copolymer, a curing agent having a bisphenol residue, a particulate filler containing zinc oxide, and an aminosiloxane, the fluorocarbon thermoplastic random copolymer having subunits of: —(CH2CF2)x—, —(CF2CF(CF3)y—, and —(CF2CF2)z—, wherein  x is from 1 to 50 or 60 to 80 mole percent,  y is from 10 to 90 mole percent,  z is from 10 to 90 mole percent,  x+y+z equals 100 mole percent; and (c) curing the coating composition for 3 to 10 hours at a temperature in the range of 220° C. to 280° C. and for an additional 2 to 10 hours at a temperature in the range of 250° C. to 270° C.

Abstract: A fuser member comprising a support and a layer overlying the support, the layer including a fluorocarbon thermoplastic random copolymer, a curing agent having a bisphenol residue, a particulate filler containing zinc oxide, an aminosiloxane, and antimony-doped tin oxide particles, the cured fluorocarbon thermoplastics random copolymer having subunits of: -(CH2CF2)x-, -(CF2CF(CF3)y-, and -(CF2CF2)z-, wherein x is from 1 to 50 or 60 to 80 mole percent, y is from 10 to 90 mole percent, z is from 10 to 90 mole percent, and x+y+z equal 100 mole percent.

Abstract: A fuser member having a support metallic core and a layer of material formed over the metallic core, the layer including composite material, including aluminum powder; a cross-linked poly(dialkylsiloxane) incorporating an oxide, wherein the poly(dialkylsiloxane) has a weight average molecular weight before crosslinking of about 5,000 to 80,000; and a silane crosslinking agent.

Abstract: A roller for use in a fusing assembly for receiving a polymeric release agent including a core and multiple layers secured over the core; and the multiple layers including at least one outer layer formed of a silicone mixture which absorbs the polymeric release agent and has toner release properties, and an intermediate layer formed of a silicone mixture selected so that its swelling in 1000 cts poly(dimethylsiloxane) is less than 1% by weight.

Abstract: The toner fuser roll of the present invention, which is characterized by good thermal conductivity and resistance to degradation by release agents in addition to excellent wear properties, is capable of producing toner fused images with desirably high gloss. In accordance with the invention, the fuser roll comprises a cylindrical core and a base cushion layer comprising a condensation-cured poly(dimethylsiloxane) elastomer formed on the core. A barrier layer that comprises a cured fluorocarbon polymer and includes a particulate filler overlies the cushion layer. Overlying the barrier layer is a highly smooth outer surface layer comprising an addition-cured poly(dimethylsiloxane) elastomer and having a roughness value, Ra, no greater than about 10 microinches. Further in accordance with the invention is a process for forming the just described toner fuser roll.

Abstract: In a fusing assembly for fixing toner to a receiver and having a fuser roller and a pressure roller forming a fixing nip, a metering roller, a polymeric release agent is applied to the metering roller and a release agent donor roller for receiving polymeric release agent from the metering roller and applying it to the surface of the fusing roller, the release agent donor roller comprising an outer layer including a silicone material selected so that its swelling in 1000 cts poly(dimethylsiloxane) is less than 6% by weight.

Abstract: A fuser member useful for heat-fixing an electrographic toner to a substrate. The fuser member has a core and a layer overlying the core. That layer includes a cured fluorocarbon random copolymer having subunits with the general structures: where x is from 30 to 90 mole percent, y is from 10 to 70 mole percent, and z is from 0 to 34 mole percent. The layer incorporates particulate filler. The filler includes aluminum oxide and a material selected from the group consisting of alkaline earth metal oxides, alkaline earth metal hydroxides, and combinations thereof. The filler has a total concentration in the layer of from about 25 to 50 percent of the total volume of the layer. The aluminum oxide has a concentration of from 20 to 40 percent of the total volume of the layer.