Abstract: A method of preparing a fluoroelastomer capable of being vulcanized by using peroxide, the method comprising: in the presence of an initiator and a chain transfer agent, conducting emulsion polymerization reaction on comonomers to obtain a fluoroelastomer. The preparation method utilizes alkyl iodide RIx as the chain transfer agent, and introduces the atom I into the molecular structure of the polymer during the reaction, the atom I acting as a crosslinking point during peroxide vulcanization. The fluoroelastomer obtained via the preparation method greatly improves the performance after being vulcanized; in addition, due to the low cost and extensive sources of alkyl iodide, the preparation method also simplifies the manufacturing process, reduces cost, and has wide application prospects.

Abstract: A method of preparing a fluoroelastomer capable of being vulcanized by using peroxide, the method comprising: in the presence of an initiator and a chain transfer agent, conducting emulsion polymerization reaction on comonomers to obtain a fluoroelastomer. The preparation method utilizes alkyl iodide RIx as the chain transfer agent, and introduces the atom I into the molecular structure of the polymer during the reaction, the atom I acting as a crosslinking point during peroxide vulcanization. The fluoroelastomer obtained via the preparation method greatly improves the performance after being vulcanized; in addition, due to the low cost and extensive sources of alkyl iodide, the preparation method also simplifies the manufacturing process, reduces cost, and has wide application prospects.

Abstract: The present invention provides a low-temperature-resistant fluorine-containing elastomer formed through polymerization of the comonomers: 40-80 mol % 1,1-vinylidene fluoride, 2-10 mol % tetrafluoroethylene, 10-30 mol % perfluoro(alkyl vinyl ether), and 1-10 mol % vulcanization monomer. The present invention further provides a preparation method of the fluorine-containing elastomer. In the present invention, on basis of a large number of experiments, the contents of the comonomers of the fluorine-containing elastomer are adjusted, so that the low temperature performance thereof is significantly improved, and the low-temperature retraction temperature TR-10<?40. Moreover, the rate of the volume change of the fluorine-containing elastomer in methanol decreases, and the oil resistance and the solvent resistance are improved, thereby improving the oil resistant performance and solvent resistant performance of the fluorine-containing elastomer.