Abstract: An essentially lead free steel having improved machinability while reducing or eliminating lead (except for trace impurities) and without detriment of the material properties of the steel. The properties of the lead free steel are dependent on both the composition and method of manufacture. The improved lead free steel has, in percent by weight (wt-%): Carbon: 0.39-0.43%; Manganese: 0.75-1.00%; Silicon: 0.15-0.35%; Chromium: 0.80-1.05%; Molybdenum: 0.15-0.25%; at least one of Tellurium: 0.003-0.090 wt-%, Selenium: 0.080-0.2 wt-%, Sulfur: 0.065-0.09% wt-%, and Bismuth: 0.03-0.1 wt-%; and the balance being Fe and normally occurring scrap steel impurities. The hot-rolled lead-free steel product is subjected to a heat treatment at a first temperature for a first duration, at a second temperature for a second duration that is less than the first temperature, at a third temperature for a third time period that is greater than the second temperature, and subsequently cooling the steel product.

Abstract: An essentially lead free steel having, in percent by weight (wt-%): Carbon: 0.39-0.43%; Manganese: 0.75-1.00%; Silicon: 0.15-0.35%; Chromium: 0.80-1.05%; Molybdenum: 0.15-0.25%; at least one of Tellurium: 0.003-0.090 wt-%, Selenium: 0.080-0.2 wt-%, Sulfur: 0.065-0.09% wt-%, and Bismuth: 0.03-0.1 wt-%; and the balance being Fe and normally occurring scrap steel impurities. A method for manufacturing an essentially lead free steel by subjecting a hot-rolled steel product to a heat treatment in which the steel product is subjected to a first temperature for a first duration; the steel product is subjected to a second temperature for a second duration, wherein the second temperature is less than the first temperature; and the steel product is subjected to a third temperature for a third time period, wherein the third temperature is greater than the second temperature; and cooling the steel product. After the heat treatment the steel is cold worked to the desired size.

Abstract: An essentially lead free steel having, in percent by weight (wt-%): Carbon: 0.39-0.43%; Manganese: 0.75-1.00%; Silicon: 0.15-0.35%; Chromium: 0.80-1.05%; Molybdenum: 0.15-0.25%; at least one of Tellurium: 0.003-0.090 wt-%, Selenium: 0.080-0.2 wt-%, Sulfur: 0.065-0.09% wt-%, and Bismuth: 0.03-0.1 wt-%; and the balance being Fe and normally occurring scrap steel impurities. A method for manufacturing an essentially lead free steel by subjecting a hot-rolled steel product to a heat treatment in which the steel product is subjected to a first temperature for a first duration; the steel product is subjected to a second temperature for a second duration, wherein the second temperature is less than the first temperature; and the steel product is subjected to a third temperature for a third time period, wherein the third temperature is greater than the second temperature; and cooling the steel product. After the heat treatment the steel is cold worked to the desired size.

Abstract: An essentially lead free steel having, in percent by weight (wt-%): Carbon: 0.39-0.43%; Manganese: 0.75-1.00%; Silicon: 0.15-0.35%; Chromium: 0.80-1.05%; Molybdenum: 0.15-0.25%; at least one of Tellurium: 0.003-0.090 wt-%, Selenium: 0.080-0.2 wt-%, Sulfur: 0.065-0.09% wt-%, and Bismuth: 0.03-0.1 wt-%; and the balance being Fe and normally occurring scrap steel impurities. A method for manufacturing an essentially lead free steel by subjecting a hot-rolled steel product to a heat treatment in which the steel product is subjected to a first temperature for a first duration; the steel product is subjected to a second temperature for a second duration, wherein the second temperature is less than the first temperature; and the steel product is subjected to a third temperature for a third time period, wherein the third temperature is greater than the second temperature; and cooling the steel product. After the heat treatment the steel is cold worked to the desired size.