Abstract: The present disclosure relates to an aluminum-based plated steel that is provided for vehicles by hot forming, an aluminum-based alloy plated steel manufactured using the same, and method of manufacturing thereof.

Abstract: The present disclosure provides a hot-press formed part comprising a plated steel sheet and an aluminum alloy plated layer formed on the plated steel sheet, wherein the aluminum alloy plated layer comprises: an alloying layer (I) formed on the plated steel sheet and containing, by weight %, 5-30% of Al; an alloying layer (II) formed on the alloying layer (I) and containing, by weight %, 30 to 60% of Al; an alloying layer (III) formed on the alloying layer (II) and containing, by weight %, 20-50% of Al and 5-20% of Si; and an alloying layer (IV) formed continuously or discontinuously on at least a part of the surface of the alloying layer (III), and containing 30-60% of Al, wherein the rate of the alloying layer (III) exposed on the outermost surface of the aluminum alloy plated layer is 10% or more.

Abstract: The present disclosure relates to an aluminum-based plated steel that is provided for vehicles by hot forming, an aluminum-based alloy plated steel manufactured using the same, and method of manufacturing thereof.

Abstract: An aspect of the present invention relates to a cold-rolled steel plate for hot forming, which is excellent in corrosion-resistance and spot-weldability, contains, by weight %, C: 0.1-0.4%, Si: 0.5-2.0%, Mn: 0.01-4.0%, Al: 0.001-0.4%, P: 0.001-0.05%, S: 0.0001-0.02%, Cr: 0.5% to less than 3.0%, N: 0.001-0.02%, and a balance of Fe and inevitable impurities, satisfying formula (1) below, and includes an Si amorphous oxidation layer continuously or discontinuously formed at a thickness of 1 nm-100 nm on the surface thereof. Formula (1): 1.4?0.4*Cr+Si?3.2 (wherein element symbols denote measurements of respective element contents by weight %).

Abstract: The present invention provides a steel sheet plated with aluminum-iron and a preparation method therefor, the steel sheet comprising: a base steel sheet; and a plated layer formed on the surface of the base steel sheet and comprising: an alloyed layer containing at least one of Fe3Al, FeAl(Si), Fe2Al5, and FeAl3; and an aluminum layer formed on the alloyed layer and having a thickness less than 10% of that of the plated layer, wherein the plated layer is 20-35 ?m in thickness and contains 1-20 wt % of Mg as measured by GDS at a position 0.1 ?m deep from the surface of the plated layer and 10 wt % of oxygen as measured by GDS at a position 0.1 ?m deep from the surface of the plated layer.

Abstract: The present disclosure provides a hot-press formed part comprising a plated steel sheet and an aluminum alloy plated layer formed on the plated steel sheet, wherein the aluminum alloy plated layer comprises: an alloying layer (I) formed on the plated steel sheet and containing, by weight %, 5-30% of Al; an alloying layer (II) formed on the alloying layer (I) and containing, by weight %, 30 to 60% of Al; an alloying layer (III) formed on the alloying layer (II) and containing, by weight %, 20-50% of Al and 5-20% of Si; and an alloying layer (IV) formed continuously or discontinuously on at least a part of the surface of the alloying layer (III), and containing 30-60% of Al, wherein the rate of the alloying layer (III) exposed on the outermost surface of the aluminum alloy plated layer is 10% or more.

Abstract: The present invention provides an iron-aluminum-based plated steel sheet, and a manufacturing method therefor, the iron-aluminum-based plated steel sheet comprising a base steel sheet and a plated layer formed on the surface of the base steel sheet, wherein the alloy plated layer comprises: a diffusion layer comprising an Fe—Al-based intermetallic compound having a cubic structure; and an alloyed layer formed on the diffusion layer and composed of an alloy phase differing from that of the cubic structure, the thickness of the diffusion layer is 3-20 ?m, and the thickness of the diffusion layer is greater than 50% of the total thickness of the plated layer.

Abstract: A method of manufacturing a steel sheet plated with an Al—Fe alloy for hot forming. The method includes: aluminum-plating and coiling a base steel sheet to obtain an aluminum-plated steel sheet, where an amount of the aluminum-plating is 30 to 200 g/m2 based on one surface of the base steel sheet, and tension in the coiling is 0.5 to 5 kg/mm2; after the aluminum-plating, performing cooling to 250° C. at a rate of 20° C./sec or less; annealing the aluminum-plated steel sheet to obtain the steel sheet plated with the Al—Fe alloy; and cooling the steel sheet plated with the Al—Fe alloy. The annealing is carried out for 30 minutes to 50 hours within a heating temperature range of 550 to 750° C. in a batch annealing furnace.

Abstract: A steel plate plated with an aluminum-iron alloy for hot press forming can include a base steel sheet and an alloy plated layer formed on the base steel sheet. The alloy plated layer can include an alloyed layer (I) formed on the base steel sheet and containing, by weight, Al: 5-30%; an alloyed layer (II) formed on the alloyed layer (I) and containing, by weight, Al: 30-60%; and an alloyed layer (III) formed on the alloyed layer (II) and containing, by weight, Al: 20-50%. The alloy layer (II) can have a FeAl (Si) alloy phase dispersed and distributed therein, in which the FeAl (Si) alloy phase includes, by weight, Al: 20-50% and Si: 5-20%, and the number density of the FeAl (Si) alloy phase having a circle-equivalent diameter of 5 ?m or less 15 is 103/mm2 or more.

Abstract: An embodiment of the present invention provides steel for hot forming, a hot-formed member, and methods for manufacturing same, the steel comprising, by wt %, 0.06-0.1% of C, 0.05-0.6% of Si, 0.6-2% of Mn, 0.05% or less of P, 0.02% or less of S, 0.01-0.1% of Al, 0.01-0.8% of Cr, 0.01-0.5% of Mo, 0.02% or less of N, and the remainder of Fe and inevitable impurities, wherein an alloy factor represented by relational expression 1 below is 7 or more, and the number of carbides having a circular equivalent diameter of 0.5 ?m or greater is 105/mm2 or less. Alloy factor=I(Mn)×I(Si)×I(Cr)×I(Mo)??[Relational expression 1] where the I values for the components are I(Mn)=3.34×Mn+1, I(Si)=0.7×Si+1, I(Cr)=2.16×Cr+1, and I(Mo)=3×Mo+1, respectively, and the content of each component is expressed as wt %.

Abstract: The present invention provides a steel sheet plated with aluminum-iron and a preparation method therefor, the steel sheet comprising: a base steel sheet; and a plated layer formed on the surface of the base steel sheet and comprising: an alloyed layer containing at least one of Fe3Al, FeAl(Si), Fe2Al5, and FeAl3; and an aluminum layer formed on the alloyed layer and having a thickness less than 10% of that of the plated layer, wherein the plated layer is 20-35 ?m in thickness and contains 1-20 wt % of Mg as measured by GDS at a position 0.1 ?m deep from the surface of the plated layer and 10 wt % of oxygen as measured by GDS at a position 0.1 ?m deep from the surface of the plated layer.

Abstract: An aspect of the present invention relates to a cold-rolled steel plate for hot forming, which is excellent in corrosion-resistance and spot-weldability, contains, by weight %, C: 0.1-0.4%, Si: 0.5-2.0%, Mn: 0.01-4.0%, Al: 0.001-0.4%, P: 0.001-0.05%, S: 0.0001-0.02%, Cr: 0.5% to less than 3.0%, N: 0.001-0.02%, and a balance of Fe and inevitable impurities, satisfying formula (1) below, and includes an Si amorphous oxidation layer continuously or discontinuously formed at a thickness of 1 nm-100 nm on the surface thereof. Formula (1): 1.4?0.4*Cr+Si?3.

Abstract: The present invention provides an iron-aluminum-based plated steel sheet, and a manufacturing method therefor, the iron-aluminum-based plated steel sheet comprising a base steel sheet and a plated layer formed on the surface of the base steel sheet, wherein the alloy plated layer comprises: a diffusion layer comprising an Fe—Al-based intermetallic compound having a cubic structure; and an alloyed layer formed on the diffusion layer and composed of an alloy phase differing from that of the cubic structure, the thickness of the diffusion layer is 3-20 ?m, and the thickness of the diffusion layer is greater than 50% of the total thickness of the plated layer.

Abstract: Provided is a cold-rolled steel plate for hot forming, which is excellent in corrosion-resistance and spot-weldability, contains, by weight %, C: 0.1-0.4%, Si: 0.5-2.0%, Mn: 0.01-4.0%, Al: 0.001-0.4%, P: 0.001-0.05%, S: 0.0001-0.02%, Cr: 0.5% to less than 3.0%, N: 0.001-0.02%, and a balance of Fe and inevitable impurities, satisfying formula (1) below, and includes an Si amorphous oxidation layer continuously or discontinuously formed at a thickness of 1 nm-100 nm on the surface thereof. Formula (1): 1.4?0.4*Cr+Si?3.2 (wherein element symbols denote measurements of respective element contents by weight %).

Abstract: Provided is a steel sheet for a hot press formed member having excellent resistance to hydrogen delayed fracture, and a method for manufacturing the same. A steel sheet for a hot press formed member comprises: a base steel sheet; an aluminum alloy plating layer on a surface of the base steel sheet; and an oxide layer which is formed on a surface of the plating layer and has a thickness of 0.05 ?m or more.

Abstract: One aspect of the present invention relates to a plated steel sheet for hot press forming, having an excellent impact property.

Abstract: Provided is a steel sheet for a hot press formed member having excellent resistance to hydrogen delayed fracture, and a method for manufacturing the same. A steel sheet for a hot press formed member comprises: a base steel sheet; an aluminum alloy plating layer on a surface of the base steel sheet; and an oxide layer which is formed on a surface of the plating layer and has a thickness of 0.05 ?m or more.

Abstract: Provided is a plated steel sheet for hot press forming, having an excellent impact property, including: a base steel sheet comprising, by wt %, 0.15-0.4% of C, 0.05-1.0% of Si, 0.6-3.0% of Mn, 0.001-0.05% of P, 0.0001-0.02% of S, 0.01-0.1% of Al, 0.001-0.02% of N, 0.001-0.01% of B, 0.01-0.5% of Cr, 0.01-0.05% of Ti, and the balance of Fe and inevitable impurities; and an Al—Si plated layer formed on the surface of the base steel sheet. A thickness of a carbon-depleted layer in a surface layer part of the base steel sheet is 5 ?m or less. The surface layer part means a region from the surface of the base steel sheet to a depth of 200 ?m, and the carbon-depleted layer means a region which the carbon content is 50% or less of an average carbon amount (C0) of the base steel sheet.

Abstract: The present invention relates to a steel sheet for a hot press formed member having excellent coating adhesion, and a method for manufacturing the same. A steel sheet for hot press forming according to one aspect of the present invention is an aluminum alloy plated steel sheet, wherein an average Fe content in a plating layer may be 40 wt % or more, and a concentration gradient of a section having a Fe content of 45 wt % to 80 wt % in the plating layer may 7 wt %/?m or less of a concentration gradient at a section having an Fe content of 45% to 80% in the plating layer in a thickness direction from a surface of the plating layer according to a result of GDS analysis.

Abstract: The present invention provides an aluminum-based plated steel plate used in hot-press forming, the steel plate comprising: a base steel plate; and a plating layer formed on the base steel plate, wherein the plating layer comprises: an alloying layer formed on the surface of the base steel plate and including one or more of Fe 3Al, FeAl(Si), Fe 2Al 5, and FeAl 3; and an aluminum layer formed on the alloying layer and having a thickness less than 10% of the thickness of the plating layer, and the plating layer has a thickness of 5-20 ?m and an oxygen content of 10 weight % or less, as measured by GDS, at a depth of 0.1 ?m from the surface of the plating layer.