Abstract: The present invention relates to a polyetherimide composite nanofiltration membrane and a preparation method thereof, the method comprises the following steps: (1) dissolving polyetherimide and an additive into an organic solvent, stirring and keeping aside for deaeration to prepare a casting solution, blade coating of the casting solution onto a smooth surface of a nonwoven fabric, and placing under an air atmosphere and then putting into deionized water to obtain a support membrane 1, wherein the surface of the nonwoven fabric coated with the casting solution is referred to as surface A; (2) immersing the surface A of the support membrane 1 into an aqueous solution of m-phenylenediamine, taking out and drying in the air, then immersing the surface A into a solution of 1,2,4,5-benzene tetracarbonyl chloride in n-hexane or cyclohexane, and taking out and drying in the air to obtain a support membrane 2; and (3) immersing the surface A of the support membrane 2 into an aqueous solution of EDC.

Abstract: The present invention relates to a polyetherimide composite nanofiltration membrane and a preparation method thereof, the method comprises the following steps: (1) dissolving polyetherimide and an additive into an organic solvent, stirring and keeping aside for deaeration to prepare a casting solution, blade coating of the casting solution onto a smooth surface of a nonwoven fabric, and placing under an air atmosphere and then putting into deionized water to obtain a support membrane 1, wherein the surface of the nonwoven fabric coated with the casting solution is referred to as surface A; (2) immersing the surface A of the support membrane 1 into an aqueous solution of m-phenylenediamine, taking out and drying in the air, then immersing the surface A into a solution of 1,2,4,5-benzene tetracarbonyl chloride in n-hexane or cyclohexane, and taking out and drying in the air to obtain a support membrane 2; and (3) immersing the surface A of the support membrane 2 into an aqueous solution of EDC.

Abstract: Disclosed is a refined white ceramic material, which belongs to the field of ceramic materials for component packaging, and comprises the following raw materials by weight in percentage: aluminum oxide 87-93, magnesium oxide 0.8-5, silicon dioxide 1-6, calcium oxide 0.6-4, titanium dioxide 0.01-0.5, and zirconium dioxide 0.5-3. The method for preparing same comprises: (1) washing aluminum oxide grinding balls and a ball-milling tank, and drying for later use; (2) weighing a solvent NP-10 of 0.5-4 by weight in percentage, and adding the solvent into the ball-milling tank; (3) weighing raw materials, adding the raw materials into the ball-milling tank, and performing ball milling for 72±0.5 h. By means of the refined white ceramic material of the present invention, the obtained ceramic grains have even sizes, small surface roughness, and high fracture resistance performance of ceramic body.

Abstract: Disclosed is a refined white ceramic material, which belongs to the field of ceramic materials for component packaging, and comprises the following raw materials by weight in percentage: aluminum oxide 87-93, magnesium oxide 0.8-5, silicon dioxide 1-6, calcium oxide 0.6-4, titanium dioxide 0.01-0.5, and zirconium dioxide 0.5-3. The method for preparing same comprises: (1) washing aluminum oxide grinding balls and a ball-milling tank, and drying for later use; (2) weighing a solvent NP-10 of 0.5-4 by weight in percentage, and adding the solvent into the ball-milling tank; (3) weighing raw materials, adding the raw materials into the ball-milling tank, and performing ball milling for 72±0.5 h. By means of the refined white ceramic material of the present invention, the obtained ceramic grains have even sizes, small surface roughness, and high fracture resistance performance of ceramic body.

Abstract: The present invention provides a high corrosion resistant aluminum alloy consisting essentially of (by weight %): 0.30-1.25% Mn, 0.10-1.20% Si, 0.05-0.25% Cr, 0.05-0.2% Zr, 0.08-0.30% Ti, less than 0.03% Zn, less than 0.03% Cu, and up to 0.20% Fe, balance aluminum and inevitable impurities. The present invention also relates to articles made of the alloy.