Abstract: A type O foot-and-mouth disease virus-like particle antigen is provided, wherein the type O foot-and-mouth disease virus-like particle antigen is type O CATHAY topotype foot-and-mouth disease virus-like particle antigen, and the type O CATHAY topotype foot-and-mouth disease virus-like particle antigen is assembled by VP0, VP3 and VP1 antigen proteins of type O CATHAY topotype foot-and-mouth disease virus. The type O foot-and-mouth disease virus-like particle antigen has good immunogenicity. The prepared vaccine can produce complete protection against the O-type foot-and-mouth disease virus on the 14th day after immunization. The antibody titer produced is higher than that of the commercial inactivated vaccine, and the duration of immune protection can be maintained for at least 133 days. The prepared vaccine composition, preparation method and use thereof are also provided.

Abstract: The present invention relates to a method for preparing an aluminum-copper-iron quasicrystal and silicon carbide mixed reinforced aluminum matrix composite, where the aluminum-copper-iron quasicrystal and silicon carbide mixed reinforced aluminum matrix composite is prepared with an aluminum alloy serving as a matrix and with aluminum-copper-iron quasicrystal and silicon carbide serving as reinforcement agents via smelting in an intermediate-frequency induction melting furnace through the process of intermediate-frequency induction heating, vacuumizing, bottom blowing argon, and casting molding in view of low hardness and low tensile strength of aluminum matrix materials. The prepared aluminum-copper-iron quasicrystal and silicon carbide mixed reinforced aluminum matrix composite has a hardness of 80.3 HB which is improved by 50.64% and tensile strength of 285 Mpa which is improved by 60.42%, and corrosion resistance thereof is improved by 40%.

Abstract: The present invention relates to a method for preparing an aluminum-copper-iron quasicrystal and silicon carbide mixed reinforced aluminum matrix composite, where the aluminum-copper-iron quasicrystal and silicon carbide mixed reinforced aluminum matrix composite is prepared with an aluminum alloy serving as a matrix and with aluminum-copper-iron quasicrystal and silicon carbide serving as reinforcement agents via smelting in an intermediate-frequency induction melting furnace through the process of intermediate-frequency induction heating, vacuumizing, bottom blowing argon, and casting molding in view of low hardness and low tensile strength of aluminum matrix materials. The prepared aluminum-copper-iron quasicrystal and silicon carbide mixed reinforced aluminum matrix composite has a hardness of 80.3 HB which is improved by 50.64% and tensile strength of 285 Mpa which is improved by 60.42%, and corrosion resistance thereof is improved by 40%.