Abstract: A peelable heat-shrink tubing includes a base polymer comprising fluorinated ethylene propylene (FEP), and at least one fluoropolymer coextruded with the base polymer. The peelable heat-shrink tubing may have a haze between about 40% and 80%, inclusive, and/or a total luminous transmittance between about 70% and 85%, inclusive. In some embodiments, the haze may be between about 50% and 70%, inclusive, and/or the total luminous transmittance may be less than about 80%. The base polymer may comprise FEP NP-130 and constitute between about 87.5% and 92.5% by composition of the peelable heat-shrink tubing, inclusive, and the at least one fluoropolymer may comprise ethylene tetrafluoroethylene (ETFE) and constitute between about 7.5% and 12.5% by composition of the peelable heat-shrink tubing, inclusively. In some embodiments, the at least one fluoropolymer may comprise 7.5% of ETFE and 5% of perfluoroalkoxy alkane (PFA), each by composition of the peelable heat-shrink tubing, inclusive.

Abstract: A method for making an expanded, and optionally multi-component and/or colored PTFE monofilament is disclosed. The method includes forming a first paste by mixing a PTFE powder with a hydrocarbon solvent; forming an extrusion preform by pressing the first paste into a form; curing the extrusion preform by exposing the extrusion preform to a first temperature for a first time duration; forming a green monofilament by extruding the first paste through a die; expanding the green monofilament by exposing the green monofilament to a second temperature for a second time duration, the second time duration occurring after the first time duration; stretching the green monofilament substantially along a longitudinal axis of the green monofilament, the stretching the green monofilament occurring after the expanding the green monofilament; and sintering the green monofilament after the stretching the green monofilament.

Abstract: A method for making an expanded, and optionally multi-component and/or colored PTFE monofilament is disclosed. The method includes forming a first paste by mixing a PTFE powder with a hydrocarbon solvent; forming an extrusion preform by pressing the first paste into a form; curing the extrusion preform by exposing the extrusion preform to a first temperature for a first time duration; forming a green monofilament by extruding the first paste through a die; expanding the green monofilament by exposing the green monofilament to a second temperature for a second time duration, the second time duration occurring after the first time duration; stretching the green monofilament substantially along a longitudinal axis of the green monofilament, the stretching the green monofilament occurring after the expanding the green monofilament; and sintering the green monofilament after the stretching the green monofilament.

Abstract: A method for making an expanded, and optionally multi-component and/or colored PTFE monofilament is disclosed. The method includes forming a first paste by mixing a PTFE powder with a hydrocarbon solvent; forming an extrusion preform by pressing the first paste into a form; curing the extrusion preform by exposing the extrusion preform to a first temperature for a first time duration; forming a green monofilament by extruding the first paste through a die; expanding the green monofilament by exposing the green monofilament to a second temperature for a second time duration, the second time duration occurring after the first time duration; stretching the green monofilament substantially along a longitudinal axis of the green monofilament, the stretching the green monofilament occurring after the expanding the green monofilament; and sintering the green monofilament after the stretching the green monofilament.

Abstract: A method for making an expanded, and optionally multi-component and/or colored PTFE monofilament is disclosed. The method includes forming a first paste by mixing a PTFE powder with a hydrocarbon solvent; forming an extrusion preform by pressing the first paste into a form; curing the extrusion preform by exposing the extrusion preform to a first temperature for a first time duration; forming a green monofilament by extruding the first paste through a die; expanding the green monofilament by exposing the green monofilament to a second temperature for a second time duration, the second time duration occurring after the first time duration; stretching the green monofilament substantially along a longitudinal axis of the green monofilament, the stretching the green monofilament occurring after the expanding the green monofilament; and sintering the green monofilament after the stretching the green monofilament.

Abstract: This invention provides security articles comprising fibers, threads and fiber sections (“dots”) possessing multiple verification characteristics. The fibers possess unique and difficulty duplicated combinations of complex cross-sections, components, and multiple luminescent responses. The many verifiable characteristics of the security fibers, threads and dots provide high levels of protection against fraudulent duplication of articles in which they are incorporated. The manifold security features provide means of tailoring specific identity characteristics for specific use and users.

Abstract: This invention provides security articles comprising fibers, threads and fiber sections (“dots”) possessing multiple verification characteristics. The fibers possess unique and difficulty duplicated combinations of complex cross-sections, components, and multiple luminescent responses. The many verifiable characteristics of the security fibers, threads and dots provide high levels of protection against fraudulent duplication of articles in which they are incorporated. The manifold security features provide means of tailoring specific identity characteristics for specific use and users.

Abstract: This invention provides security articles comprising fibers, threads and fiber sections (“dots”) possessing multiple verification characteristics. The fibers possess unique and difficulty duplicated combinations of complex cross-sections, components, and multiple luminescent responses. The many verifiable characteristics of the security fibers, threads and dots provide high levels of protection against fraudulent duplication of articles in which they are incorporated. The manifold security features provide means of tailoring specific identity characteristics for specific use and users.

Abstract: A yarn having good entanglement and good quality, preferably a multifilament polyamide yarn, a method for making the yarn, and a woven fabric made from the yarn wherein the yarn comprises the following properties: the yarn length per defect is greater than or equal to about 3000 meters per defect; the maximum skip length is less than or equal to about 120 millimeters; the ratio between yarn length per defect to maximum skip length is greater than or equal to about 50; the entanglements per meter times the average entanglement strength is greater than or equal to about 120; and the yarn can be woven sizeless. The yarn of the invention is useful in the sizeless weaving of fabric used in air bags.

Abstract: A yarn having good entanglement and good quality, preferably a multifilament polyamide yarn, a method for making the yarn, and a woven fabric made from the yarn wherein the yarn comprises the following properties: the yarn length per defect is greater than or equal to about 3000 meters per defect; the maximum skip length is less than or equal to about 120 millimeters; the ratio between yarn length per defect to maximum skip length is greater than or equal to about 50; the entanglements per meter times the average entanglement strength is greater than or equal to about 120; and the yarn can be woven sizeless. The yarn of the invention is useful in the sizeless weaving of fabric used in air bags.

Abstract: This invention provides security articles comprising fibers, threads and fiber sections (“dots”) possessing multiple verification characteristics. The fibers possess unique and difficulty duplicated combinations of complex cross-sections, components, and multiple luminescent responses. The many verifiable characteristics of the security fibers, threads and dots provide high levels of protection against fraudulent duplication of articles in which they are incorporated. The manifold security features provide means of tailoring specific identity characteristics for specific use and users.

Abstract: A yarn having good entanglement and good quality, preferably a multifilament polyamide yarn, a method for making the yarn, and a woven fabric made from the yarn wherein the yarn comprises the following properties: the yarn length per defect is greater than or equal to about 3000 meters per defect; the maximum skip length is less than or equal to about 120 millimeters; the ratio between yarn length per defect to maximum skip length is greater than or equal to about 50; the entanglements per meter times the average entanglement strength is greater than or equal to about 120; and the yarn can be woven sizeless. The yarn of the invention is useful in the sizeless weaving of fabric used in air bags.

Abstract: A yarn having good entanglement and good quality, preferably a multifilament polyamide yarn, a method for making the yarn, and a woven fabric made from the yarn wherein the yarn comprises the following properties: the yarn length per defect is greater than or equal to about 3000 meters per defect; the maximum skip length is less than or equal to about 120 millimeters; the ratio between yarn length per defect to maximum skip length is greater than or equal to about 50; the entanglements per meter times the average entanglement strength is greater than or equal to about 120; and the yarn can be woven sizeless. The yarn of the invention is useful in the sizeless weaving of fabric used in air bags.

Abstract: Ultra-oriented, crystalline synthetic filaments with a combination of high tenacity, high dimensional stability, high modulus, and a high fraction of taut-tie molecular phase are produced by extruding a fiber-forming synthetic polymer melt into a liquid isothermal bath, withdrawing the filaments from the bath and then post-treating them at a very low draw ratio. The bath is preferably maintained at a temperature of at least 30.degree. C. above the glass transition temperature of the polymer to enhance the orientation and promote the formation of stable extended chains. Polymer filaments so produced are characterized in that they have ultra-high birefringence, high tenacity and modulus, a high dimensional stability, and a high fraction of taut-tie molecular phase.

Abstract: This invention provides security articles comprising fibers, threads and fiber sections (“dots”) possessing multiple verification characteristics. The fibers possess unique and difficulty duplicated combinations of complex cross-sections, components, and multiple luminescent responses. The many verifiable characteristics of the security fibers, threads and dots provide high levels of protection against fraudulent duplication of articles in which they are incorporated. The manifold security features provide means of tailoring specific identity characteristics for specific use and users.