Abstract: A rubber composition has an improved rolling resistance and is based on at least a diene elastomer comprising mainly at least one isoprene elastomer; a reinforcing filler comprising from 15 to 70 phr of carbon black having a BET specific surface area of less than 70 m2/g, and/or a COAN of less than 90 ml/100 g, and from 5 to 20 phr of silica; a salt of an alkaline-earth, alkali or lanthanide metal; and a crosslinking system; in which composition the carbon black to silica ratio is greater than 1.

Abstract: The present disclosure relates to tires, at least one internal layer of which exhibits good mechanical properties and reduced rolling resistance, the said internal layer comprising a rubber composition based on at least 80 to 100 phr of an isoprene elastomer, a reinforcing filler predominantly comprising carbon black, 1 to 45 phr of reinforcing resin, a salt of an alkaline earth, alkali or lanthanide metal, and a crosslinking system.

Abstract: A rubber composition has an improved rolling resistance and is based on at least a diene elastomer comprising mainly at least one isoprene elastomer; a reinforcing filler comprising from 15 to 70 phr of carbon black having a BET specific surface area of less than 70 m2/g, and/or a COAN of less than 90 ml/100 g, and from 5 to 20 phr of silica; a salt of an alkaline-earth, alkali or lanthanide metal; and a crosslinking system; in which composition the carbon black to silica ratio is greater than 1.

Abstract: The invention relates to aA rubber composition has an improved rolling resistance and is based on at least a diene elastomer comprising mainly at least one isoprene elastomer; a reinforcing filler comprising from 10 to 35 phr of carbon black having a BET specific surface area of less than 70 m2/g, and from 10 to 40 phr of silica; a coupling agent in a content corresponding to a range extending from 5 to 15% by weight relative to the weight of silica; and a crosslinking system; in which composition the total content of carbon black and silica is between 20 and 70 phr, and in which the carbon black to silica weight ratio is greater than 0.3.

Abstract: A rubber composition has an improved rolling resistance and is based on at least a diene elastomer comprising mainly at least one isoprene elastomer; a reinforcing filler comprising from 5 to 60 phr of carbon black having a BET specific surface area of less than 70 m2/g, termed coarse carbon black, and from 10 to 30 phr of carbon black having a BET specific surface area of greater than or equal to 70 m2/g, termed fine carbon black; a salt of an alkali, alkaline-earth or lanthanide metal; and a crosslinking system.

Abstract: The crosslinkable rubber composition comprises a first elastomer consisting of polybutadiene having a Mooney plasticity ranging from 40 to 70 Mooney units, the content of the first elastomer being strictly greater than 50 phr, a second elastomer, and a carbon black having a specific surface area within a range of values extending from 15 m2/g to 25 m2/g and an oil adsorption number of compressed sample (COAN) within a range of values extending from 65 ml/100 g to 85 ml/100 g.

Abstract: The crosslinkable rubber composition comprises a first elastomer consisting of polybutadiene having a Mooney plasticity ranging from 40 to 70 Mooney units, the content of the first elastomer being strictly greater than 50 phr, a second elastomer, and a carbon black having a specific surface area within a range of values extending from 15 m2/g to 25 m2/g and an oil adsorption number of compressed sample (COAN) within a range of values extending from 65 ml/100 g to 85 ml/100 g.