Abstract: The present invention provides a mixture comprising at least three hardener components a1), a2), and b), the ratio of hardener component a1) to a2) being in the range from 0.1 to 10:1, and hardener component b) being present at 5% to 55% by weight, based on the mixture, a process for preparing this mixture, the use of the mixture of the invention for curing epoxy resins, the use of the mixture of the invention with epoxy resins as adhesives, and an epoxy resin cured with the mixture of the invention.

Abstract: The present invention provides a blend comprising one or more epoxy resins and a mixture which comprises 0.3 to 0.9 amine equivalent, per equivalent of epoxide of the epoxy resin used, of a hardener component a) and as hardener component b) a compound of the formula I, a process for preparing this blend, the use of the blend of the invention for producing cured epoxy resin, and an epoxy resin cured with the blend of the invention.

Abstract: The present invention provides a process for producing moldings, the curing of the mold being carried out using a blend comprising one or more epoxy resins and a mixture, the curing component a) being used within the mixture in the range from 0.3 to 0.9 amine equivalent per equivalent of epoxide of the epoxy resin used, and the hardener component b) being a compound of the formula I.

Abstract: The present invention provides a blend comprising one or more epoxy resins and a mixture which comprises 0.3 to 0.9 amine equivalent, per equivalent of epoxide of the epoxy resin used, of a hardener component a) and as hardener component b) a compound of the formula I, a process for preparing this blend, the use of the blend of the invention for producing cured epoxy resin, and an epoxy resin cured with the blend of the invention.

Abstract: The present invention provides a blend comprising one or more epoxy resins and a mixture which comprises 0.3 to 0.9 amine equivalent, per equivalent of epoxide of the epoxy resin used, of a hardener component a) and as hardener component b) a compound of the formula I, a process for preparing this blend, the use of the blend of the invention for producing cured epoxy resin, and an epoxy resin cured with the blend of the invention.

Abstract: The present invention provides a blend comprising one or more epoxy resins and a mixture which comprises 0.3 to 0.9 amine equivalent, per equivalent of epoxide of the epoxy resin used, of a hardener component a) and as hardener component b) a compound of the formula I, a process for preparing this blend, the use of the blend of the invention for producing cured epoxy resin, and an epoxy resin cured with the blend of the invention.

Abstract: The present invention provides a process for producing moldings, the curing of the mold being carried out using a blend comprising one or more epoxy resins and a mixture, the curing component a) being used within the mixture in the range from 0.3 to 0.9 amine equivalent per equivalent of epoxide of the epoxy resin used, and the hardener component b) being a compound of the formula I.

Abstract: The present invention provides a mixture comprising at least three hardener components a1), a2), and b), the ratio of hardener component a1) to a2) being in the range from 0.1 to 10:1, and hardener component b) being present at 5% to 55% by weight, based on the mixture, a process for preparing this mixture, the use of the mixture of the invention for curing epoxy resins, the use of the mixture of the invention with epoxy resins as adhesives, and an epoxy resin cured with the mixture of the invention.

Abstract: Aqueous, autocrosslinking polymer dispersion binders comprising polyhydrazides and carbonyl-containing polyurethane-vinyl hybrid polymers and also, if desired, conventional additives, are useful in base coatings, aqueous coatings, adhesives and printing inks.

Abstract: Curing agents for aqueous epoxy resin dispersions obtained by reaction of an adduct (A) of at least one polyepoxide (A.sub.1) and at least one polyalkylene polyether polyol (A.sub.2), it being possible for the adduct (A) to be modified with a secondary amine (A.sub.3) if appropriate, withI. a reaction product of an amine (B) and an epoxide (C)orII. an amine (B) and subsequent reaction with an epoxide (C),the amount of amine (B) being chosen such that the H atoms on the nitrogen are present in a 2- to 10-fold excess, based on the epoxide groups in (A).

Abstract: Aqueous, autocrosslinking polymer dispersion binders comprising polyhydrazides and carbonyl-containing polyurethane-vinyl hybrid polymers and also, if desired, conventional additives, are useful in base coatings, aqueous coatings, adhesives and printing inks.

Abstract: Curing agents for aqueous epoxy resin dispersions obtained by reaction of an adduct (A) of at least one polyepoxide (A.sub.1) and at least one polyalkylene polyether polyol (A.sub.2), it being possible for the adduct (A) to be modified with a secondary amine (A.sub.3) if appropriate, withI. a reaction product of an amine (B) and an epoxide (C)orII. an amine (B) and subsequent reaction with an epoxide (C),the amount of amine (B) being chosen such that the H atoms on the nitrogen are present in a 2- to 10-fold excess, based on the epoxide groups in (A).

Abstract: Polyol/epoxy adducts obtained by reaction of(A) an aliphatic polyol having an average molecular weight (Mw) of 200 to 2000 and(B) an epoxy compound having at least two epoxy groups per molecule and an epoxy equivalent weight of 100 to 2000,the equivalent ratio of the OH groups to the epoxy groups being 1:3.51 to 1:10, preferably 1:4 to 1:9, particularly preferably 1:45 to 1:8, and the epoxy equivalent weight of the adduct being between 150 g/eq and at least 800 g/eq, preferably between 250 g/eq and 1000 g/eq which adducts serve as nonionic emulsifiers in water-dilutable epoxy liquid resins.

Abstract: Aqueous epoxy resin dispersions containing(A) an epoxy resin which is a condensation product of one or more epoxy compound(s), of an aromatic polyol and, if used, of a modifying compound having at least two groups which are reactive with epoxides,(B) a dispersing agent in the form of a condensation product of an aliphatic polyol and an epoxy compound, the equivalent ratio of the OH groups to the epoxy groups being 1:0.8 to 1:3.5,(C) a carboxyl-containing or -releasing curing agent for the epoxy resin comprising one or more carboxyl-containing compound(s), at least one of these compounds having a functionality of at least three carboxyl groups per molecule, and(D) if desired customary additives, components (A), (B) and (C) being used in such amounts by weight that the equivalent ratio of the epoxy groups of component (A) capable of reacting to the carboxyl groups of component (B) is at least 1:0.5.

Abstract: Crosslinked polymer microparticles based on epoxy resin obtained by polymerization of aqueous dispersions (A) of compounds containing epoxide groups in the presence of up to 0.2 mol, preferably 0.02 to 0.15 mol (based on the nitrogen contained in (B)) of a nitrogen-containing organic compound (B) per epoxide equivalent and subsequent isolation which are preferably in the form of aqueous dispersions thereof, and are suitable as organic fillers, pigments, matting agents and/or reinforcing agents for binder systems and individual components thereof, paint formulations, coating and molding compositions, intermediate coatings, adhesives and the like, preferably based on water.

Abstract: A process for the preparation of aqueous epoxy resin dispersions comprising(1) 20 to 75% by weight, based on the total dispersion, of an epoxy resin constituting a condensation product ofa) epoxy compounds having at least one epoxy group per molecule and an epoxide equivalent weight of 90 to 3000 g/mol, andb) aromatic polyols;(2) 3 to 20% by weight, based on the total dispersion, of an emulsifier comprisinga) a condensation product of an aliphatic polyol and an epoxy compound having at least two epoxy groups per molecule and an epoxide equivalent weight of 90 to 3000 g/mol, the equivalent ratio of the OH groups to the epoxy groups being 1:0.85 to 1:1.