Abstract: A colloidal suspension of LEV structure type crystalline molecular sieve, making the suspension by washing smaller crystallites from a previously found solid LEV product, and using the suspension as seeds in further crystalline molecular sieve syntheses.

Abstract: Layers comprising a molecular sieve layer on a porous or non-porous support, having uniform properties and allowing high flux are prepared from colloidal solutions of zeolite or other molecular sieve precursors (particle size less than 100 nm), by deposition, e.g., by spin or dip-coating, or by in situ crystallization.

Abstract: Colloidal crystalline molecular sieve seeds are used in phosphorus-containing crystalline molecular sieve manufacture. Certain of the products have enhanced utility in oxygenate conversions.

Abstract: A process for converting hydrocarbons by contacting a hydrocarbon feedstream under hydrocarbon conversion conditions with a large crystal zeolite catalyst. The large crystal zeolite of the catalyst used in the hydrocarbon conversion process is made by heating an aqueous zeolite synthesis mixture under agitation to a temperature equal to or less than the effective nucleation temperature of the synthesis mixture. After this step, the aqueous synthesis mixture is heated in the absence of agitation to a temperature equal to or greater than the effective nucleation temperature of the aqueous zeolite synthesis mixture. The process finds particular application in hydrocarbon conversion processes where reduced non-selective acidity is important for reaction selectivity and/or the maintenance of catalyst activity, e.g., toluene disproportionation, dealkylation, alkylation, and transalkylation.

Abstract: Large crystal zeolites are prepared by heating a zeolite synthesis mixture under agitation to a temperature equal to or less than the effective nucleation temperature of the zeolite synthesis mixture and thereafter the zeolite synthesis mixture is heated without agitation to a temperature equal to or greater than the effective nucleation temperature of the zeolite synthesis mixture.