Abstract: The electrical conductivity of a wrought processed, high strength, age hardened Be—Cu alloy is enhanced by overaging the alloy in manufacture.

Abstract: The yield strength of UNS C17460 BeCu alloy can be significantly enhanced without compromising electrical conductivity or bend formability by age hardening the alloy during manufacture using two separate heat treatment steps and cold rolling the alloy for enhancing age hardening response between these two heat treatment steps rather than before age hardening begins as in current technology.

Abstract: A higher order beryllium-nickel-copper alloy a process for making the same, and an article of manufacture comprising the alloy, the alloy being represented by the formula (0.15-0.5% Be)+(0.40-1.25% Ni)+(0-0.25% Sn)+[0.06-1% Zr) and/or (0.06-1% Ti)], the balance copper, where the sum of % Zr and % Ti is generally within a range of 0.06% and 1%, the alloy being characterized by improved electrical conductivity, bend formability and stress relaxation resistance without sacrificing strength.

Abstract: A higher order beryllium-nickel-copper alloy a process for making the same, and an article of manufacture comprising the alloy, the alloy being represented by the formula (0.15-0.5% Be) +(0.40-1.25% Ni)+(0-0.25% Sn)+[(0.06-1% Zr) and/or (0.06-1% Ti)], the balance copper, where the sum of % Zr and % Ti is generally within a range of 0.06% and 1%, the alloy being characterized by improved electrical conductivity, bend formability and stress relaxation resistance without sacrificing strength.

Abstract: A higher order beryllium-nickel-copper alloy a process for making the same, and an article of manufacture comprising the alloy, the alloy being represented by the formula (0.15-0.5% Be)+(0.40-1.25% Ni)+(0-0.25% Sn)+[(0.06-1% Zr) and/or (0.06-1% Ti)], the balance copper, where the sum of % Zr and % Ti is generally within a range of 0.06% and 1%, the alloy being characterized by improved electrical conductivity, bend formability and stress relaxation resistance without sacrificing strength.

Abstract: This invention is directed to the treatment of copper beryllium alloys, and to articles and parts made therefrom, containing special small amounts of beryllium and cobalt, e.g., about 0.2% to about 0.5% beryllium and about 0.2% to about 1% or about 1.5% or about 2% cobalt, which imparts to these alloys a superior combination of stress relaxation resistance, formability, ductility, conductivity and strength by the process of solution annealing, cold working at least about 50% or at least about 70% or 90% or more and age hardening.

Abstract: This invention is directed to the treatment of copper beryllium alloys, and to articles and parts made therefrom, containing special small amounts of beryllium and nickel, e.g., about 0.05% to about 0.5% beryllium and about 0.05% to about 1% nickel where cobalt may be substituted for up to about one-half of said nickel content at a substitution ratio of about 1 part by weight cobalt for about 2 parts by weight nickel, which imparts to these alloys a superior combination of stress relaxation resistance, formability, ductility, conductivity and strength by the process of solution annealing, cold working at least about 50% or at least about 70% or 90% or more and age hardening.

Abstract: This invention is directed to the treatment of copper beryllium alloys, and to articles and parts made therefrom, containing special small amounts of beryllium and cobalt, e.g., about 0.05% to about 0.5% beryllium and about 0.05% to about 2% cobalt, which imparts to these alloys a superior combination of stress relaxation resistance, formability, ductility, conductivity and strength by the process of solution annealing, cold working at least about 50% or at least about 70% or 90% or more and age hardening.

Abstract: This invention is directed to age hardenable copper beryllium alloys, and to articles and parts made therefrom, which contain special small amounts of beryllium and cobalt; e.g., about 0.2% to about 0.5% beryllium and about 0.2% to about 0.4% cobalt, which, when finished by solution treating, cold working at least about 50% or at least about 70% and age hardening have a superior combination of stress relaxation resistance, formability, ductility, conductivity and strength.

Abstract: Direct current inrush upon connection of a capacitive load to a d.c. voltage is limited through an intermediary circuit. Within such circuit the inrush current is sensed by a series resistance and such sensing is utilized via a feedback loop, to control a series current regulating transistor to be cyclically conducting or non-conducting of a first direct current path. A second direct current path through freewheeling diodes flows current to the load only when such series current regulating transistor is non-conducting of such first path current. After fully charging the capacitive load, howsoever slowly as desired, the first current path conducts with low power dissipation while the second current path is non-conducting. The circuit is further controlled to be correctly operative for control of inrush current during the turn-on, or disruption of, fundamental power to such circuit.