Abstract: A chemical cleaning method for cleaning an internal passage of an engine-run gas turbine engine airfoil wherein the airfoil is immersed in an inorganic hydroxide medium at superambient temperature and atmospheric pressure for a short time to remove accumulated oxides and dirt from the internal passage. The hydroxide medium can comprise molten KOH and immersion times of the engine-run airfoil not exceeding 10 minutes are involved.

Abstract: A chemical cleaning method for cleaning an internal passage of an engine-run gas turbine engine airfoil wherein the airfoil is immersed in an inorganic hydroxide medium at superambient temperature and atmospheric pressure for a short time to remove accumulated oxides and dirt from the internal passage. The hydroxide medium can comprise molten KOH and immersion times of the engine-run airfoil not exceeding 10 minutes are involved.

Abstract: Manufacture of superalloy component wherein the component is blasted with abrasive grit particles at one or more stages during the manufacture, is treated with a chemical grit removal medium effective to dissolve and remove abrasive grit particles from the surface of the component without degradation of the component (substrate), and then is coated with a protective coating such that entrapped grit particles are substantially reduced or eliminated from the coating.

Abstract: A gas turbine engine component having a thermal barrier coating is immersed in an inorganic hydroxide bath having a high concentration of alkali or alkaline earth hydroxide with the bath at ambient (atmospheric) pressure and elevated temperature for a time sufficient to effect rapid detachment of the thermal barrier coating for removal from the substrate. The component then optionally can be immersed in a water bath to remove any remaining thermal barrier coating. The thermal barrier coating is removed without detectable damage to the substrate or any bondcoat present thereon.