Abstract: The present invention provides novel biomaterials comprising one or more of Mg, Zn and F ions in a carbonate-containing biphasic calcium phosphate (BCP) system. The biomaterial may contain Mg, Zn, F, Mg and Zn, Mg and F, Zn and F, or Mg, Zn and F. The biomaterial may be substantially similar in composition to bone mineral (a carbonate apatite). The biomaterial may feature slow release of Mg, Zn, F, Ca, and P ions. The biphasic calcium phosphate, BCP, may be a mixture of unsubstituted hydroxyapatite (HA) and unsubstituted.-TCP, Ca3(PO4)2. BCP of varying HA/.-TCP ratios may be produced by sintering calcium-deficient apatite, for instance having a Ca/P<1.5, 1.6, 1.67, 1.75 or 1.8 that has been prepared either by a precipitation or by a hydrolysis method or by a solid-state reaction. The amount of each component (by weight %) present in the biomaterials may be as follows: Mg 0.5 to 12 wt %, Zn 1 to 12 wt %, F 0.1 to 4 wt %, calcium 20 to 40 wt %, phosphate 10 to 20 wt %, and carbonate (CO3) 1 to 20 wt %.

Abstract: The present invention provides novel biomaterials comprising one or more of Mg, Zn and F ions in a carbonate-containing biphasic calcium phosphate (BCP) system. The biomaterial may contain Mg, Zn, F, Mg and Zn, Mg and F, Zn and F, or Mg, Zn and F. The biomaterial may be substantially similar in composition to bone mineral (a carbonate apatite). The biomaterial may feature slow release of Mg, Zn, F, Ca, and P ions. The biphasic calcium phosphate, BCP, may be a mixture of unsubstituted hydroxyapatite (HA) and unsubstituted .-TCP, Ca3(PO4)2. BCP of varying HA/.-TCP ratios may be produced by sintering calcium-deficient apatite, for instance having a Ca/P<1.5, 1.6, 1.67, 1.75 or 1.8 that has been prepared either by a precipitation or by a hydrolysis method or by a solid-state reaction. The amount of each component (by weight %) present in the biomaterials may be as follows: Mg 0.5 to 12 wt %, Zn 1 to 12 wt %, F 0.1 to 4 wt %, calcium 20 to 40 wt %, phosphate 10 to 20 wt %, and carbonate (CO3) 1 to 20 wt %.

Abstract: A method for forming a highly adherent coating of a desired calcium phosphate phase on titanium-based substrates for use as orthopedic and dental implants. The calcium phosphate phase coating is electrochemically deposited onto the substrate from a metastable calcium phosphate electrolyte solution using a modulated electrical potential under pH, temperature and electrolyte composition and concentration conditions favorable for forming the desired calcium phosphate.