Abstract: The carrier of the present invention includes at least 85 wt percent alpha alumina, at least 0.06 wt percent SiO2 and no more than 0.04 wt percent Na2O. The carrier has a water absorption no greater than 0.35 g/g and a ratio of water absorption (g/g) to surface area (m2/g) no greater than 0.50 g/m2. Another aspect of the invention is a catalyst for the epoxidation of olefins which comprises the above described carrier and silver dispersed thereon, where the carrier has a monomodal, bimodal or multimodal pore distribution and where the quantity of silver is between 5 and 50 wt/%, relative to the weight of the catalyst. A reactor system for the epoxidation of olefins is also disclosed.

Abstract: The carrier of the present invention includes at least 85 wt percent alpha alumina, at least 0.06 wt percent SiO2 and no more than 0.04 wt percent Na2O. The carrier has a water absorption no greater than 0.35 g/g and a ratio of water absorption (g/g) to surface area (m2/g) no greater than 0.50 g/m2. Another aspect of the invention is a catalyst for the epoxidation of olefins which comprises the above described carrier and silver dispersed thereon, where the carrier has a monomodal, bimodal or multimodal pore distribution and where the quantity of silver is between 5 and 50 wt %, relative to the weight of the catalyst. A reactor system for the epoxidation of olefins is also disclosed.

Abstract: The carrier of the present invention includes at least 85 wt percent alpha alumina, at least 0.06 wt percent SiO2 and no more than 0.04 wt percent Na2O. The carrier has a water absorption no greater than 0.35 g/g and a ratio of water absorption (g/g) to surface area (m2/g) no greater than 0.50 g/m2. Another aspect of the invention is a catalyst for the epoxidation of olefins which comprises the above described carrier and silver dispersed thereon, where the carrier has a monomodal, bimodal or multimodal pore distribution and where the quantity of silver is between 5 and 50 wt %, relative to the weight of the catalyst. A reactor to system for the epoxidation of olefins is also disclosed.

Abstract: A carrier, which comprises non-platelet alumina and/or a bond material, has a surface area of at least 1.3 m2/g, a total pore volume and a pore size distribution such that at least 80% of the total pore volume is contained in pores with diameters in the range of from 0.1 to 10 ?m, and at least 80% of the pore volume contained in the pores with diameters in the range of from 0.1 to 10 ?m is contained in pores with diameters in the range of from 0.

Abstract: A carrier, which comprises non-platelet alumina and/or a bond material, has a surface area of at least 1.3 m2/g, a total pore volume and a pore size distribution such that at least 80% of the total pore volume is contained in pores with diameters in the range of from 0.1 to 10 ?m, and at least 80% of the pore volume contained in the pores with diameters in the range of from 0.1 to 10 ?m is contained in pores with diameters in the range of from 0.

Abstract: The selectivity and activity of a silver-based olefin epoxidation catalyst is found to be a function of the pore size distribution in the alumina carrier on which it is deposited. Specifically it is found advantageous to provide a carrier which has a minimum of very large pores, (greater than 10 micrometers) and a water absorption of 35 to 55% and a surface area of at least 1.0 m2/g. A method of making such carriers is also described.

Abstract: The selectivity and activity of a silver-based olefin epoxidation catalyst is found to be a function of the pore size distribution in the alumina carrier on which it is deposited. Specifically it is found advantageous to provide a carrier which has a minimum of very large pores, (greater than 10 micrometers) and a water absorption of 35 to 55% and a surface area of at least 1.0 m2/g. A method of malting such carriers is also described.

Abstract: The selectivity and activity of a silver-based olefin epoxidation catalyst is found to be a function of the pore size distribution in the alumina carrier on which it is deposited. Specifically it is found advantageous to provide a carrier which has a minimum of very large pores, (greater than 10 micrometers) and a water absorption of 35 to 55% and a surface area of at least 1.0 m2/g. A method of making such carriers is also described.