Abstract: The present invention relates to silane adducts having a relatively higher adhesive strength as expressed formula X3SiR1, and manufacturing method thereof. wherein X is a hydrogenated form selected from one of epoxy compounds, amino compounds and bisphenolic, and R1 is selected from one of glycidyloxypropyl group, 2-(3,4-epoxycyclohexyl)ethyl group, 3-acryloxypropyl group, 3-methacryloxypropyl group, amino-propyl group, 3-[2-(2-aminoethylamino)ethylamino]propyl group, N-methylaminopropyl group, N-phenylaminopropyl group, N,N-dimethyl-3-aminopropyl group, mercapto-propyl group, cyano-propyl group, and isocyanato-propyl group.

Abstract: The present invention relates to silane adducts having a relatively higher adhesive strength as expressed formula X3SiR1, and manufacturing method thereof. wherein X is a hydrogenated form selected from one of epoxy compounds, amino compounds and bisphenolic, and R1 is selected from one of glycidyloxypropyl group, 2-(3,4-epoxycyclohexyl)ethyl group, 3-acryloxypropyl group, 3-methacryloxypropyl group, amino-propyl group, 3-[2-(2-aminoethylamino)ethylamino]propyl group, N-methylaminopropyl group, N-phenylaminopropyl group, N,N-dimethyl-3-aminopropyl group, mercapto-propyl group, cyano-propyl group, and isocyanato-propyl group.

Abstract: A melt-flow controlling method for elastomer by uv irradiation for use in semiconductor packages by ultraviolet irradiation, in which a coated polymer composition is crosslinked by ultraviolet irradiation after a coating process of the polymer composition in producing the elastic adhesives. In producing the elastic adhesives for use as the thermal stress relief layer in semiconductor packages, the inventive method comprises irradiating the polymer composition with ultraviolet light of a 100-500 nm wavelength in order to control the flowability and crosslinking degree of the coated polymer composition. Thus, according to the present invention, a heating furnace is not used such that energy consumption can be reduced. Also, curing can be achieved in a short time so as to increase productivity, and the crosslinking degree is easily controlled by changing the ultraviolet dose as compared to the thermal crossliking process.

Abstract: The present invention relates to silane adducts having a relatively higher adhesive strength as expressed formula X3SiR1, and manufacturing method thereof. wherein X is a hydrogenated form selected from one of epoxy compounds, amino compounds and bisphenolic, and R1 is selected from one of glycidyloxypropyl group, 2-(3,4-epoxycyclohexyl)ethyl group, 3-acryloxypropyl group, 3-methacryloxypropyl group, amino-propyl group, 3-[2-(2-aminoethylamino)ethylamino]propyl group, N-methylaminopropyl group, N-phenylaminopropyl group, N, N-dimethyl-3-aminopropyl group, mercapto-propyl group, cyano-propyl group, and isocyanato-propyl group.