Abstract: An adhesion bond strength enhancer for cementitious adhesive mortar is disclosed. The adhesion enhancer improves bond strength between the mortar and relatively hydrophobic plastic material, such as extruded polystyrene boards and expanded polystyrene boards of the type generally employed in Exterior Insulation Finishing Systems (“EIFS”). Preparation of non-caking, free-flowing, solid dialkyl sulfosuccinate compositions for use as the adhesion enhancer is also disclosed. The adhesion enhancer is attractive for large-scale application in mineral mortar dry-mixes or other solid construction materials. The invention can be used to improve the strength of an adhesive bond between a) gypsum based plaster or stucco and concrete or bricks, b) tile adhesives and concrete, and c) mineral mortars on polystyrene boards, among others.

Abstract: An adhesion bond strength enhancer for cementitious adhesive mortar is disclosed. The adhesion enhancer improves bond strength between the mortar and relatively hydrophobic plastic material, such as extruded polystyrene boards and expanded polystyrene boards of the type generally employed in Exterior Insulation Finishing Systems (“EIFS”). Preparation of non-caking, free-flowing, solid dialkyl sulfosuccinate compositions for use as the adhesion enhancer is also disclosed. The adhesion enhancer is attractive for large-scale application in mineral mortar dry-mixes or other solid construction materials. The invention can be used to improve the strength of an adhesive bond between a) gypsum based plaster or stucco and concrete or bricks, b) tile adhesives and concrete, and c) mineral mortars on polystyrene boards, among others.

Abstract: The invention provides a process for the production of 4-(C2-C16)alkylresorcinol. 4-(C2-C16)alkylresorcinol is produced by reacting resorcinol with a (C2-C16)alkyloic acid in the presence of a zinc chloride catalyst to produce an intermediate comprising a 4-(C2-C16)acylresorcinol and zinc ions. Then the intermediate is adjusted such that the zinc ion content is from about 0.1 to about 150 parts per million based on the weight of the intermediate to form an adjusted intermediate. Then the produced 4-(C2-C16)acylresorcinol is hydrogenated in the presence of the zinc ions and a base metal hydrogenation catalyst to produce a crude product comprising 4-(C2-C16)alkylresorcinol, which may thereafter be isolated.

Abstract: A process for producing a phenothiazinium compound comprising the step of: reacting phenothiazine, in the presence of a halogen, with at least one amine selected from the group consisting of: wherein Z is CH2, O, S, SO2, NH, NCH3, NC2H5, NCH2CH2OH or NCOCH3, and R1 and R2 are each independently linear or branched CnH2nY; and replacing the halogen with a non-halide counteranion.