Abstract: The invention provides a process for producing a cement clinker comprising: (i) mixing one or more starting materials providing each at least one or more of CaO, SiO2, Al2O3, and Fe2O3; and, optionally, SO3, to form a raw meal comprising CaO, SiO2, Al2O3, and Fe2O3; and, optionally, SO3, wherein the molar ratios among the aforementioned oxides is given by Formula I: (CaO)1(SiO2)a(Al2O3)b(Fe2O3)c(SO3)d, wherein: “a” is comprised from 0.05 to 1, “b” is comprised from 0.01 to 0.6, “c” is comprised from 0.001 to 0.25, and “d” is comprised from 0 to 0.3 and wherein at least 35% (p/p) of the starting materials of the raw meal have a critical microwaves absorbance temperature (Tc) comprised from 15 to 650° C. and a critical microwaves absorbance time (tc) comprised from 1 min to 1 h; (ii) heating the raw meal by irradiating with microwaves during 15 min to 3 h to reach a sintering temperature comprised from 300 to 950° C.

Abstract: The invention provides a process for producing a cement clinker comprising: (i) mixing one or more starting materials providing each at least one or more of CaO, SiO2, AI2O3, and Fe2O3; and, optionally, SO3, to form a raw meal comprising CaO, SiO2, AI2O3, and Fe2O3; and, optionally, SO3, wherein the molar ratios among the aforementioned oxides is given by Formula I: S(CaO)1(SiO2)a(Al2O3)b(Fe2O3)c(SO3)d, wherein: “a” is comprised from 0.05 to 1, “b” is comprised from 0.1 to 0.6, “c” is comprised from 0.001 to 0.25, and “d” is comprised from 0 to 0.3 and wherein at least 35% (p/p) of the starting materials of the raw meal have a critical microwaves absorbance temperature (Tc) comprised from 15 to 650° C. and a critical microwaves absorbance time (tc) comprised from 1 min to 1 h; (ii) heating the raw meal by irradiating with microwaves during 15 min to 3 h to reach a sintering temperature comprised from 300 to 950° C.