Abstract: Dispersing agents useful in a suspension polymerization process may be formed based on polyvinyl alcohols and processes discloses herein. The dispersing agent may include, for example: a polyvinyl alcohol having a degree of hydrolysis in the range from 60 to 80 mol %; an absorbance of not less than 0.3 measured at a wavelength of 320 nm with respect to a 0.1 wt % aqueous solution of the polyvinyl alcohol; a block character of remaining ester groups in the range from 0.4 to 0.5; and a cloud point in the range from 35° C. to 50° C. measured with respect to a 1 wt % aqueous solution of the polyvinyl alcohol. Carbonyl groups are theorized to be present along the polymer chain, which may be quantified by 1-H NMR spectra peaks.

Abstract: Dispersing agents useful in a suspension polymerization process may be formed based on polyvinyl alcohols and processes discloses herein. The dispersing agent may include, for example: a polyvinyl alcohol having a degree of hydrolysis in the range from 60 to 80 mol %; an absorbance of not less than 0.3 measured at a wavelength of 320 nm with respect to a 0.1 wt % aqueous solution of the polyvinyl alcohol; a block character of remaining ester groups in the range from 0.4 to 0.5; and a cloud point in the range from 35° C. to 50° C. measured with respect to a 1 wt % aqueous solution of the polyvinyl alcohol. Carbonyl groups are theorized to be present along the polymer chain, which may be quantified by 1-H NMR spectra peaks.

Abstract: A process for manufacturing a highly water-soluble vinyl alcohol-N-vinyl amine copolymer with a degree of hydrolysis higher than 93%, including a hydrolysis reaction of a vinyl alcohol-N-vinyl formamide copolymer with an alkaline metal hydroxide in methanol wherein the process is carried out with more than 1.5 mol of the alkaline metal hydroxide per mol of N-vinyl formamide units and without addition of water. A higher water soluble vinyl alcohol-N-vinyl amine copolymer obtained by this process and the use thereof.