Abstract: An improved dry spinning process for the production of polyurethane elastomer threads using superheated steam as the spinning medium, comprising(1) spinning polyurethane-urea elastomers prepared by chain lengthening of NCO prepolymers with diamine from a solution containing dimethylformamide or dimethylacetamide via a hot spinneret having a nozzle at not less than 100.degree. C. and at a spinning solution temperature in the nozzle of not less than 100.degree. C. into a heated spinning chimney at a chimney wall temperature of not less than 160.degree. C., while(2) introducing superheated steam into the spinning chimney at a temperature above 250.degree. C. as the spinning medium in an amount of at least 20 kg/h, if the chimney diameter is less than or equal to 28 cm, or if the chimney diameter is greater than 28 cm, in an amount of at least 20 kg/h increased by up to a factor H, wherein factor H is equal to the chimney cross-section/615 cm.sup.