Abstract: There is provided a material for dentures having metallic matrix, containing 0.5-30 volume % glass having a softening temperature above 650.degree. C. and/or ceramic particles having a maximum grain size of 40 .mu.m.

Abstract: A denture with a metallic microstructure and with low shrinkage and porosity is produced by metallurgical sintering by providing a multimodal size distribution of coarse and fine fractions of metal powder, optionally also with glass or ceramic powder, converting this powder mixture with water into a slip, modelling the denture with this, and sintering the slip at a temperature which exceeds the solidus temperature of at least one component of the powder mixture.

Abstract: Low gold dental alloys, especially for firing on dental porcelains, should be easily worked, result in no discolorations and bubble formation in the firing, and have a physiologically replaceable hardness and a low melting interval. These properties are shown by alloys having 20 to 35 wt. % gold and 45 to 65 wt. % palladium if they also contain(a) 6 to 15 wt. % copper and 0 to 10 wt. % nickel,(b) 0 to 12 wt. % indium, 0 to 12 wt. % tin, and 0 to 4 wt. % gallium, with the proviso that the sum of the content of indium and tin added to two and one-half times the gallium content must give a value between 5 and 15 wt. %,(c) 0.1 to 1 wt. % iridium and/or rhenium and/or ruthenium, and(d) optionally 0 to 1 wt. % aluminum, 0 to 1 wt. % tantalum, 0 to 1 wt. % titanium and/or 0 to 5 wt. % silver.