Abstract: A sealing glass composition in powdered form comprising a crystallizable base glass in the vitreous state and vanadium zirconium silicate in an amount from about 0.1 to 1 weight percent of the base glass. The sealing glass also may contain aluminum oxide having a particle size of about 90 to 99 percent minus 325 mesh in an amount from about 0.1 to 1.0 weight percent of the base glass and bismuth nitrate in an amount from about 0.02 to 0.08 weight percent of the base glass. The glass composition can be used to seal cathode ray tube face plates and funnels with excellent results when heated to a hold range of about 4300 C to 4500 C. The crystallized sealing glass exhibits improved adhesion to seal edges of the face plates and funnels, increased strength, and improved resistance to organic contamination.