Abstract: A straightforward and scalable solid-state synthesis at 975° C. used to generate cathode materials in the system Li(3+x)3Ni(1-x-y)CoyMn2x/3O2 {a combination of LiNiO2, Li2MnO3, and LiCoO2 as (1-x-y)LiNiO2.xLi2MnO3.yLiCoO2} is described. Coatings for improving the characteristics of the cathode material are also described. A ternary composition diagram was used to select sample points, and compositions for testing were initially chosen in an arrangement conducive to mathematical modeling. X-ray diffraction (XRD) characterization showed the formation of an ?-NaFeO2 structure, except in the region of compositions close to LiNiO2. Electrochemical testing revealed a wide range of electrochemical capacities with the highest capacities found in a region of high Li2MnO3 content. The highest capacity composition identified was Li1.222Mn0.444Ni0.167Co0.167O2 with a maximum initial discharge capacity of in the voltage range 4.6-2.0 V.