Abstract: The present invention provides a water-based black ink, utilizing biochar as the black pigment. The black inks of the invention contain high bio-renewable carbon content (BRC), preferably 100% BRC. The inks exhibit the physical properties required to perform according to the requirements of rotogravure and flexographic printing.

Abstract: The present invention provides a water-based black ink, utilizing biochar as the black pigment. The black inks of the invention contain high bio-renewable carbon content (BRC), preferably 100% BRC. The inks exhibit the physical properties required to perform according to the requirements of rotogravure and flexographic printing.

Abstract: Described herein is a polar non-aqueous dispersion comprising polar polymeric microparticles in a polar non-aqueous medium, the polar polymeric microparticles being insoluble in the medium and being produced by dispersion polymerization of vinyl monomers such as acrylate monomers in the medium in the presence of a polymeric acrylic stabilizer. Inks, coatings and overprint varnishes are formulated that employ the polar non-aqueous dispersion. Such inks, etc., exhibit superior chemical resistance properties, for example in one-part and two-part systems.

Abstract: The present invention provides novel anionic modified rosin ester resins having a high BRC content, up to 100% BRC. The resins of the present invention are useful as emulsion, dispersion, or solution resins. High BRC content pigment grind vehicles, coatings, and finished inks can be prepared using the resins of the present invention. Advantageously, the finished inks of the present invention have equal to or superior properties compared to current commercially available inks sold as sustainable products, but having little to no BRC content. The present invention represents a significant step towards developing sustainable inks and coatings that are better for the environment.

Abstract: Described herein is a polar non-aqueous dispersion comprising polar polymeric microparticles in a polar non-aqueous medium, the polar polymeric microparticles being insoluble in the medium and being produced by dispersion polymerization of vinyl monomers such as acrylate monomers in the medium in the presence of a polymeric acrylic stabilizer. Inks, coatings and overprint varnishes are formulated that employ the polar non-aqueous dispersion. Such inks, etc., exhibit superior chemical resistance properties, for example in one-part and two-part systems.

Abstract: Provided are retort inks containing binder, colorant and carrier, where the cured ink has a bond strength to a layer of retort material of at least about 500 g/2.54 cm before retorting and/or the binder has an endotherm of 0.6 J/g or less or after retorting a bond strength of at least about 375 g/2.54 cm or destruct strength. Laminate plies carrying the ink and retorts using the ink also are provided.

Abstract: Provided are retort inks containing binder, colorant and carrier, where the cured ink has a bond strength to a layer of retort material of at least about 500 g/2.54 cm before retorting and/or the binder has an endotherm of 0.6 J/g or less or after retorting a bond strength of at least about 375 g/2.54 cm or destruct strength. Laminate plies carrying the ink and retorts using the ink also are provided.

Abstract: Provided are retort inks containing binder, colorant and carrier, where the cured ink has a bond strength to a layer of retort material of at least about 500 g/2.54 cm before retorting and/or the binder has an endotherm of 0.6 J/g or less or after retorting a bond strength of at least about 375 g/2.54 cm or destruct strength. Laminate plies carrying the ink and retorts using the ink also are provided.

Abstract: A retort ink contains binder, colorant and carrier and the cured ink has a bond strength to a layer of retort material of at least about 500 g/2.54 cm before retorting and/or the binder has an endotherm of 0.6 J/g or less or after retorting a bond strength of at least about 375 g/2.54 cm or destruct strength. Laminate plies carrying the ink and retorts using the ink are described.

Abstract: A process for preparing a terpene-phenol resin with a softening point in the range of from about 80.degree. C. to about 110.degree. C. The method comprises preparing a reaction mixture including a terpene, phenol and a complex of boron trifluoride. The boron trifluoride complex is selected from the group consisting of a ether complex of boron trifluoride, wherein the ether has an molecular weight in the range of from about 46 to about 140, and an organic acid complex of boron trifluoride, wherein the organic acid has a molecular weight in the range of from about 46 to about 300. The reaction mixture is maintained at a temperature in the range of from about 50.degree. C. to about 90.degree. C. for a period of time sufficient to produce the .alpha.-pinene-phenol resin which is then recovered from the reaction mixture. The terpene may be selected from the group consisting of .alpha.-pinene, .beta.-pinene, .delta.-3-carene, dipentene, limonene and mixtures of those terpenes.