Abstract: A positive electrode slurry composition includes a positive electrode active material, a binder, a dispersant, and a solvent, wherein the positive electrode active material includes lithium iron phosphate including a carbon coating layer on the surface thereof, and the binder includes polyvinylidene fluoride satisfying the following Expression 1 0?{(2A+B)/(C+D)}×100<0.2??[Expression 1] wherein A, B, C, and D are the integrated areas of respective peaks exhibited at 11.5 ppm to 12.8 ppm, 3.9 ppm to 4.2 ppm, 2.6 ppm to 3.2 ppm, and 2.1 ppm to 2.35 ppm as measured by 1H-NMR of the polyvinylidene fluoride.

Abstract: A positive electrode slurry composition includes a positive electrode active material, a conductive material, a binder, a dispersant, and a solvent, wherein the positive electrode active material includes lithium iron phosphate, the lithium iron phosphate has an average particle diameter D50 of 1.5 ?m or more, and the dispersant is included in an amount of 0.2 parts by weight to 0.9 parts by weight with respect to 100 parts by weight of solids in the positive electrode slurry composition.

Abstract: A positive electrode slurry composition includes a positive electrode active material, a dispersant, a conductive material, a binder, and a solvent, wherein the positive electrode active material includes lithium iron phosphate, and the dispersant has a weight-average molecular weight of 10,000 g/mol to 150,000 g/mol.

Abstract: The present invention relates to a method of welding an electrode tab which welds an electrode tab and a current collecting layer by using a pulsed laser beam, and a cable type rechargeable battery including an electrode manufactured according to the same.

Abstract: Provided is a method for manufacturing a flexible electrode, including the steps of: (i) coating a porous current collector having a plurality of pores with an active material slurry having a solid content of 30-50% and drying the active material slurry to form an active material coating layer; (ii) coating an active material slurry having a solid content of 30-50% on the active material coating layer formed from the preceding step and drying the active material slurry to form an additional active material coating layer; and (iii) repeating step (ii) n times (1?n?5) to form multiple active material coating layers, thereby forming an electrode active material layer in the pores and on the surface of the porous current collector in a non-press mode. A flexible electrode obtained from the method and a lithium secondary battery including the flexible electrode are also provided.

Abstract: Provided is a packaging for a flexible secondary battery, including: a first polymer resin layer; a barrier layer formed on the first polymer resin layer for interrupting moisture and gases; a parylene layer including parylene on at least one surface of the barrier layer; and a second polymer resin layer formed on the barrier layer, wherein the parylene layer has a thickness of 0.1-2.5 ?m. A flexible secondary battery including the packaging is also provided.

Abstract: Provided is a packaging for a flexible secondary battery, including: a first polymer resin layer; a barrier layer formed on the first polymer resin layer for interrupting moisture and gases; a parylene layer including parylene on at least one surface of the barrier layer; and a second polymer resin layer formed on the barrier layer, wherein the parylene layer has a thickness of 0.1-2.5 ?m. A flexible secondary battery including the packaging is also provided.

Abstract: The present invention relates to a method of welding an electrode tab which welds an electrode tab and a current collecting layer by using a pulsed laser beam, and a cable type rechargeable battery including an electrode manufactured according to the same.

Abstract: Provided is a method for manufacturing a flexible electrode, including the steps of: (i) coating a porous current collector having a plurality of pores with an active material slurry having a solid content of 30-50% and drying the active material slurry to form an active material coating layer; (ii) coating an active material slurry having a solid content of 30-50% on the active material coating layer formed from the preceding step and drying the active material slurry to form an additional active material coating layer; and (iii) repeating step (ii) n times (1?n?5) to form multiple active material coating layers, thereby forming an electrode active material layer in the pores and on the surface of the porous current collector in a non-press mode. A flexible electrode obtained from the method and a lithium secondary battery including the flexible electrode are also provided.

Abstract: A method for manufacturing a lithium secondary battery including (S1) providing a battery frame including a battery casing, the battery casing including a first side and a second side, the first side including a three-dimensional porous positive electrode current collector and the second side including a three-dimensional porous negative electrode current collector; (S2) introducing a positive electrode active material to the pores formed in the positive electrode current collector, and introducing a negative electrode active material to the pores formed in the negative electrode current collector; and (S3) pressing the battery casing to deform the battery casing into a predetermined shape.