Abstract: The method of making a supercapacitor using porous activated carbon from cow dung includes converting cow dung to porous activated carbon by, in a first step, preparing the dung waste by washing and drying the dung waste, and heating the dung waste in a vacuum environment to form pre-carbonized carbon. In a second step, the pre-carbonized carbon is impregnated with phosphoric acid to form a slurry, which is dried, ground, and heated in a vacuum to between 600-900° C. to form porous activated carbon. The porous activated carbon is mixed with a binder, acetylene black, and an organic solvent to form a paste, which is dried on a conductive metal foil to form an electrode. Two such electrodes (an anode and cathode) to are coated with an electrolyte gel (e.g., aqueous potassium hydroxide) and separated by a polymer (e.g., PTFE) membrane to form the supercapacitor.

Abstract: The method of making a supercapacitor using porous activated carbon from cow dung includes converting cow dung to porous activated carbon by, in a first step, preparing the dung waste by washing and drying the dung waste, and heating the dung waste in a vacuum environment to form pre-carbonized carbon. In a second step, the pre-carbonized carbon is impregnated with phosphoric acid to form a slurry, which is dried, ground, and heated in a vacuum to between 600-900° C. to form porous activated carbon. The porous activated carbon is mixed with a binder, acetylene black, and an organic solvent to form a paste, which is dried on a conductive metal foil to form an electrode. Two such electrodes (an anode and cathode) to are coated with an electrolyte gel (e.g., aqueous potassium hydroxide) and separated by a polymer (e.g., PTFE) membrane to form the supercapacitor.

Abstract: The method of making a supercapacitor using porous activated carbon from cow dung includes converting cow dung to porous activated carbon by, in a first step, preparing the dung waste by washing and drying the dung waste, and heating the dung waste in a vacuum environment to form pre-carbonized carbon. In a second step, the pre-carbonized carbon is impregnated with phosphoric acid to form a slurry, which is dried, ground, and heated in a vacuum to between 600-900° C. to form porous activated carbon. The porous activated carbon is mixed with a binder, acetylene black, and an organic solvent to form a paste, which is dried on a conductive metal foil to form an electrode. Two such electrodes (an anode and cathode) are coated with an electrolyte gel (e.g., aqueous potassium hydroxide) and separated by a polymer (e.g., PTFE) membrane to form the supercapacitor.