Abstract: A workpiece with transport porosity is formed. Nanopores are formed in the workpiece by a thermochemical treatment. The workpiece is formed as a rigid carbonaceous skeleton containing in its structure particles of one or more carbides, being selected and arranged in order to provide predetermined nanopore sizes, a predetermined volume of nanopores and a predetermined distribution of nanopores within the volume of the article dependent on its intended use.

Abstract: The present invention relates to a method for producing a porous carbon article comprising the steps of forming a workpiece with transport porosity and forming nanopores in said workpiece by thermochemical treatment. According to the invention the workpiece is formed as a rigid carbonaceous skeleton containing in its structure particles of one or more carbides, being selected and arranged in order to provide predetermined nanopore sizes, a predetermined volume of nanopores and a predetermined distribution of nanopores within the volume of the article.

Abstract: An electrode comprising a carbon material with a solid carbon skeleton network and a capacitor containing same, in which there is a first and a second plurality of pores forming transport channels and the first plurality of pores have a pore size of less than 10 nm.

Abstract: A process of manufacturing a porous carbon material and a capacitor having the same is provided. The process is comprised of: forming an intermediate blank (in the shape of a desired electrode) made of a metal carbide material having a porosity in the range of substantially 30% to 50% by volume. The blank is then impregnated by exposure to a gaseous hydrocarbon mixture at a temperature exceeding the decomposition of the hydrocarbon until the mass of the blank increases by about 10% to 25%. Next the inner surface of the blank is activated by heating. The blank is then exposed to gaseous chlorine and heated to remove the metal and form the blank having transport channels. Further chlorination occurs which forms nano sized pores in the structure. Thus, a porous carbon material is made which contains transport channels and nano sized pores.