Abstract: The invention relates to an aqueously dispersible polyurethane having a specific amount of substance of hydroxyl groups, —OH, of at least 0.6 mol/kg, and additionally satisfying at least two of the following conditions: a) a degree of branching measured as specific amount of substance of tertiary and/or quaternary aliphatic carbon atoms of from 0.01 mol/kg to 0.5 mol/kg, b) a specific amount of urea groups >N—CO—N< of from 0.8 mol/kg to 2 mol/kg, and c) a specific amount of substance of hydroxyl groups, —OH, of from 1 mol/kg to 4 mol/kg, wherein in each case the specific amount of substance is based on the mass of the polyurethane, a process for the preparation thereof, and a method of use thereof.

Abstract: The invention relates to an aqueously dispersible polyurethane having a specific amount of substance of hydroxyl groups, —OH, of at least 0.6 mol/kg, and additionally satisfying at least two of the following conditions: a) a degree of branching measured as specific amount of substance of tertiary and/or quaternary aliphatic carbon atoms of from 0.01 mol/kg to 0.5 mol/kg, b) a specific amount of urea groups >N—CO—N< of from 0.8 mol/kg to 2 mol/kg, and c) a specific amount of substance of hydroxyl groups, —OH, of from 1 mol/kg to 4 mol/kg, wherein in each case the specific amount of substance is based on the mass of the polyurethane, a process for the preparation thereof, and a method of use thereof.

Abstract: Water-dilutable polyurethane resins with acid groups, wherein the polyurethane resins contain units derived from oils A which are at least partly unsaturated, from olefinically unsaturated aliphatic acids B or anhydrides B? thereof, from compounds C having functional groups which are reactive towards acid groups or acid anhydride groups, selected from the group consisting of epoxide groups, hydroxyl groups, mercaptan groups and amino groups, and which react in the reaction with the compounds B or B? to form an ester group, a thioester group or an acid amide group, where the compounds C are selected from the group consisting of compounds C? which additionally contain sulfonic acid groups, or carboxylic acid groups which are activated by electron-withdrawing substituents, and compounds C? which additionally contain at least one hydroxyl group which is retained during the reaction with the compounds B or B?, and where at least a mass fraction of 25% of the compounds C consists of compounds C?, and polyfunctional

Abstract: The invention relates to self-crosslinking aqueous polyurethane dispersions containing a crosslinking agent I selected from diamones I1 and dihydrazides I2, and polyurethanes comprising structural elements derived from polyisocyanates A, polyols B having a number average molar mass Mn of at least 400 g/mol, compounds D comprising at least two groups which are reactive compared to isocyanate groups and at least one group able to form anions, low-molecular polyols E that carry no other reactive groups compared to isocyanate groups, compounds F containing at least one group which is reactive compared to isocyanate, and at least one aldehyde-type or ketone-type carbonyl group, and compounds G that are monofunctional compared to isocyanates or contain active hydrogen with different capabilities of reaction and are different from the compounds E. The invention also relates to methods for the production of said dispersions, and coating agents containing the same.

Abstract: Water-dilutable polyurethane dispersions comprising structural units derived from polyisocyanates A, polyols B having a number-average molar mass Mn of at least 400 g/mol, compounds D that contain at least two groups reactive towards isocyanate groups and at least one group capable of anion formation, low molar mass polyols E that do not carry any further groups reactive towards isocyanate groups, compounds G that are monofunctional towards isocyanates or contain active hydrogen of different reactivity and that are different from the compounds E, characterised in that the polyols B contain a mass fraction of polycarbonate polyols B1 of at least 85%, and the use thereof in coating compositions

Abstract: The invention relates to self-crosslinking aqueous polyurethane dispersions containing a crosslinking agent I selected from diamones I1 and dihydrazides I2, and polyurethanes comprising structural elements derived from polyisocyanates A, polyols B having a number average molar mass Mn of at least 400 g/mol, compounds D comprising at least two groups which are reactive compared to isocyanate groups and at least one group able to form anions, low-molecular polyols E that carry no other reactive groups compared to isocyanate groups, compounds F containing at least one group which is reactive compared to isocyanate, and at least one aldehyde-type or ketone-type carbonyl group, and compounds G that are monofunctional compared to isocyanates or contain active hydrogen with different capabilities of reaction and are different from the compounds E. The invention also relates to methods for the production of said dispersions, and coating agents containing the same.

Abstract: Water-dilutable polyurethane dispersions comprising structural units derived from polyisocyanates A, polyols B having a number-average molar mass Mn of at least 400 g/mol, compounds D that contain at least two groups reactive towards isocyanate groups and at least one group capable of anion formation, low molar mass polyols E that do not carry any further groups reactive towards isocyanate groups, compounds G that are monofunctional towards isocyanates or contain active hydrogen of different reactivity and that are different from the compounds E, characterised in that the polyols B contain a mass fraction of polycarbonate polyols B1 of at least 85%, and the use thereof in coating compositions

Abstract: Aqueous stoving enamels containing resins A which have hydroxyl groups and are made hydrophilic by partially neutralized acid groups, and highly etherified aminoplasts B, characterised in that the aqueous solutions or dispersions of the resin have a pH value of 6 or below, a method for the preparation thereof, and a method of use comprising coating thermally sensitive substrates.

Abstract: A water-dispersible polyurethane resin comprising building blocks derived from polyisocyanates A, polyols B having a number-average molar mass Mn of at least 400 g/mol, where appropriate, low molar mass polyols C with Mn below 400 g/mol, compounds D which possess at least two groups which are reactive toward isocyanate groups and at least one group which is capable of forming anions, low molar mass polyols E which in relation to isocyanate groups carry no further reactive groups, compounds F, which are monofunctional toward isocyanates or contain active hydrogen of different reactivity and are different from the compounds E and also, where appropriate, compounds G, which are different from B, C, D, E and F and contain at least two groups which are reactive with NCO groups, wherein the number-average molar mass Mn of the polyurethane resin is at least 10 kg/mol, its weight-average molar mass Mw is at least 20 kg/mol, and its acid number is from 20 to 50 mg/g; a process for its preparation; and its use as a bin

Abstract: A water-dilutable polyester resin ABCD having a mass fraction of from 1 to 10% of units derived from unsaturated cocondensed building blocks, an olefinic double bond content of from 10 to 2 000 mmol/kg, and a sulfonic acid group content of from 20 to 300 mmol/kg, modified if desired by copolymerizing olefinically unsaturated monomers in the presence of the polyester resin, a process for preparing them, and their use in particular in one-component coating compositions in combination with amino resin curatives.

Abstract: The invention relates to aqueous coating compositions with an anti-tarnish effect, containing a water-soluble or dispersed binding agent A and a compound B selected from fatty acid esters, containing hydroxyl groups of multivalent alcohols, and also to the use thereof for tarnish-protected glazings.

Abstract: Aqueous stoving enamels containing resins A which have hydroxyl groups and are made hydrophilic by partially neutralized acid groups, and highly etherified aminoplasts B, characterised in that the aqueous solutions or dispersions of the resin have a pH value of 6 or below, a method for the preparation thereof, and a method of use comprising coating thermally sensitive substrates

Abstract: Coating composition especially for preparing automotive surfacers, comprising a condensation product A of a carboxyl-containing resin A1 and a hydroxyl-containing resin A2, a curing agent C which becomes active only at an elevated temperature of at least 80° C., and a high molecular mass polyurethane B.

Abstract: A water-dilutable polyester resin ABCD having a mass fraction of from 1 to 10% of units derived from unsaturated cocondensed building blocks, an olefinic double bond content of from 10 to 2 000 mmol/kg, and a sulfonic acid group content of from 20 to 300 mmol/kg, modified if desired by copolymerizing olefinically unsaturated monomers in the presence of the polyester resin, a process for preparing them, and their use in particular in one-component coating compositions in combination with amino resin curatives

Abstract: Aqueous coating compositions comprising polycarbonate polyols A2 and a polyurethane chain-extended with compounds D which are at least difunctional with respect to isocyanates, said polyurethane comprising building blocks of hydroxy acids C and urethane groups derived from polyfunctional isocyanates B, wherein the polyurethane contains blocks derived from polyene polyols A1 and from polycarbonate polyols A2; a process for preparing them; and a method of use thereof for the preparation of “soft feel” coatings

Abstract: An aqueous dispersion comprising a high molar mass polyurethane A and additives B, wherein the polyurethane has a number-average molar mass of at least 10 kg/mol and a weight-average molar mass of at least 20 kg/mol and wherein the additives B contain mercaptan groups, hydrazide groups and/or N-alkylamide groups, their preparation, and their use as a surface protection coating, especially for motor vehicles.

Abstract: Coating composition especially for preparing automotive surfacers, comprising a condensation product A of a carboxyl-containing resin A1 and a hydroxyl-containing resin A2, a curing agent C which becomes active only at an elevated temperature of at least 80 ° C.

Abstract: A water-dispersible polyurethane resin comprising building blocks derived from polyisocyanates A, polyols B having a number-average molar mass Mn of at least 400 g/mol, where appropriate, low molar mass polyols C with Mn below 400 g/mol, compounds D which possess at least two groups which are reactive toward isocyanate groups and at least one group which is capable of forming anions, low molar mass polyols E which in relation to isocyanate groups carry no further reactive groups, compounds F, which are monofunctional toward isocyanates or contain active hydrogen of different reactivity and are different from the compounds E and also, where appropriate, compounds G, which are different from B, C, D, E and F and contain at least two groups which are reactive with NCO groups, wherein the number-average molar mass Mn of the polyurethane resin is at least 10 kg/mol, its weight-average molar mass Mw is at least 20 kg/mol, and its acid number is from 20 to 50 mg/g; a process for its preparation; and its use as a bin

Abstract: Storage-stable polyurethane dispersions preparable by reacting polydienes A which carry at least two isocyanate-reactive groups, polyols B which carry at least one acid group, polyfunctional isocyanates C and chain extenders D, wherein the acid groups of the polyols B are neutralized to a fraction of from 60 to 95%, processes for preparing them, and their use for producing elastic coatings.

Abstract: Water dilutable binder for soft feel coating materials, comprising an aqueous dispersion of a hydroxyl-containing polyester-urethane A, preparable by reacting a polyester A1 with hydroxyl groups as functional groups, formed from difunctional or polyfunctional carboxylic acids A11 and difunctional or polyfunctional alcohols A12, with a polyfunctional isocyanate A2, with a compound A3 having at least one isocyanate-reactive group and at least one acid group, an aqueous solution or dispersion of a triazine resin B, wherein the glass transition temperature of the polyester-urethane A is between −70 and −20° C. and wherein the hydroxyl number of the polyester-urethane A is from 10 to 120 mg/g, a process for its preparation, and its use in soft feel coating materials for plastics, metals, glass, wood, textiles, and leather.