Abstract: It is an object of the present invention to provide a filter having excellent filtration rate and excellent permeability and a method for producing the same. To achieve the above object, the present invention provides a filter comprising a porous metal support having the first pore size; and a metal coating layer formed on the support and having the second pore size smaller than the first pore size, wherein the coating layer has a three-dimensional pore structure by bonding flake-shaped metal powders. The present invention also provides a method for producing the filter. According to the present invention, as the flake-shaped second powders form a coating layer, the porosity increases and the permeability increases, and as the flow channel becomes more complicated, the filtration rate also increases.

Abstract: It is an object of the present invention to provide a filter having excellent filtration rate and excellent permeability and a method for producing the same. To achieve the above object, the present invention provides a filter comprising a porous metal support having the first pore size; and a metal coating layer formed on the support and having the second pore size smaller than the first pore size, wherein the coating layer has a three-dimensional pore structure by bonding flake-shaped metal powders. The present invention also provides a method for producing the filter. According to the present invention, as the flake-shaped second powders form a coating layer, the porosity increases and the permeability increases, and as the flow channel becomes more complicated, the filtration rate also increases.

Abstract: The present invention provides a method for manufacturing an aluminum electrode using a solution process and an aluminum electrode manufactured thereby. The manufacturing method includes the steps of: manufacturing an aluminum precursor solution for the solution processing using AlH3 as a basic material before forming aluminum; coating the aluminum precursor solution on a substrate through the solution process and drying the aluminum precursor solution; and forming a low work function aluminum electrode through a low-temperature baking process at the temperature of at most 150° C. The method for manufacturing the aluminum electrode according to the present invention improves a thermal defect of the electrode due to a high-temperature baking process, prevents excessive loss of raw materials, and can manufacture aluminum electrodes of various sizes with area ranging from small to large at relatively low costs and by a simple process under atmospheric pressure.

Abstract: The present disclosure provides a composite heat-dissipation substrate and a method of manufacturing the same. The composite heat-dissipation substrate includes a first ceramic layer having insulating properties, a second porous ceramic layer and a metal layer, wherein the first ceramic layer and the second ceramic layer are continuously connected to each other so as not to form an interface therebetween, and the metal layer is infiltrated into plural pores of the second ceramic layer to be coupled to the ceramic layers, whereby interfacial coupling force between the ceramic layers and the metal layer is very high, thereby providing significantly improved heat dissipation characteristics.

Abstract: The present disclosure provides a composite heat-dissipation substrate and a method of manufacturing the same. The composite heat-dissipation substrate includes a first ceramic layer having insulating properties, a second porous ceramic layer and a metal layer, wherein the first ceramic layer and the second ceramic layer are continuously connected to each other so as not to form an interface therebetween, and the metal layer is infiltrated into plural pores of the second ceramic layer to be coupled to the ceramic layers, whereby interfacial coupling force between the ceramic layers and the metal layer is very high, thereby providing significantly improved heat dissipation characteristics.

Abstract: The present disclosure provides a composite heat-dissipation substrate and a method of manufacturing the same. The composite heat-dissipation substrate includes a first ceramic layer having insulating properties, a second porous ceramic layer and a metal layer, wherein the first ceramic layer and the second ceramic layer are continuously connected to each other so as not to form an interface therebetween, and the metal layer is infiltrated into plural pores of the second ceramic layer to be coupled to the ceramic layers, whereby interfacial coupling force between the ceramic layers and the metal layer is very high, thereby providing significantly improved heat dissipation characteristics.

Abstract: The present invention provides a method for manufacturing an aluminum electrode using a solution process and an aluminum electrode manufactured thereby. The manufacturing method includes the steps of: manufacturing an aluminum precursor solution for the solution processing using AlH3 as a basic material before forming aluminum; coating the aluminum precursor solution on a substrate through the solution process and drying the aluminum precursor solution; and forming a low work function aluminum electrode through a low-temperature baking process at the temperature of at most 150° C. The method for manufacturing the aluminum electrode according to the present invention improves a thermal defect of the electrode due to a high-temperature baking process, prevents excessive loss of raw materials, and can manufacture aluminum electrodes of various sizes with area ranging from small to large at relatively low costs and by a simple process under atmospheric pressure.

Abstract: A nano-size lead-free piezoceramic powder and a method of mechanochemically synthesizing the same are provided. The nano-size lead-free piezoceramic powder can have a basic component of (KxNa1-x)NbO3, where x ranges from 0 to 1. A weight ratio of a milling ball to a raw powder can be set, and then the milling ball and the raw powder can be provided into a milling container at the set ratio. Nano-size lead-free piezoceramic powder can be mechanochemically synthesized using a high-energy ball mill device.

Abstract: A porous molybdenum disilicide-based material prepared by preheating a preform consisting of size-controlled molybdenum (Mo) powder and content-controlled silicon (Si) powder and igniting the preform to initiate self-propagating high temperature synthesis, and a method for preparing the same, are disclosed. The method comprises the steps of a) mixing molybdenum (Mo) powder and silicon (Si) powder in the stoichiometric ratio of 1:2; b) molding the mixed powder into a preform; c) preheating the preform under inert atmosphere; and d) igniting the top end of the preheated perform. The porous molybdenum disilicide-based material can control its pore size by appropriately controlling the size of molybdenum (Mo) powder, the content of silicon (Si) powder and preheating condition. Therefore, since the pore size gradient of the porous material is possible to form, the porous material can be used for filters with improved dirt-holding capacity.

Abstract: A porous molybdenum disilicide-based material prepared by preheating a preform consisting of size-controlled molybdenum (Mo) powder and content-controlled silicon (Si) powder and igniting the preform to initiate self-propagating high temperature synthesis, and a method for preparing the same, are disclosed. The method comprises the steps of a) mixing molybdenum (Mo) powder and silicon (Si) powder in the stoichiometric ratio of 1:2; b) molding the mixed powder into a preform; c) preheating the preform under inert atmosphere; and d) igniting the top end of the preheated perform. The porous molybdenum disilicide-based material can control its pore size by appropriately controlling the size of molybdenum (Mo) powder, the content of silicon (Si) powder and preheating condition. Therefore, since the pore size gradient of the porous material is possible to form, the porous material can be used for filters with improved dirt-holding capacity.