Abstract: The present invention provides a high-performance lithium-containing organic sulfur electrode material and a preparation method of an integrated flexible electrode. According to the present invention, 1,3-diisopropenyl benzene with diene bonds and Li2S6 are used as precursors to react to generate the lithium-containing organic sulfide Poly (Li2S6-r-DIB) through an in-situ polymerization method. The synthesized lithium-containing organic sulfide Poly (Li2S6-r-DIB) can be directly attached to a flexible conductive carbon cloth to prepare the integrated flexible electrode due to its good viscosity when heated to a certain temperature. The obtained flexible electrode has the advantages of high capacity, high flexibility, stable structure and the like.

Abstract: The invention discloses a method for preparing graphene oxide quantum dots in a large scale with cryptocrystalline graphite, comprising the following steps: mixing a certain amount of cryptocrystalline graphite powder, sodium nitrate, and sulfuric acid with ultrasonic treating; stirring the solution for 1-3 hours in ice-water bath; adding a certain amount of potassium permanganate, and mixing while stirring, then increasing temperature; adding deionized water, increasing the temperature and maintain for 1-3 hours, then diluting with water and adding a certain amount of hydrogen peroxide, stirring followed by standing and staying overnight; adding hydrochloric solution; adding water into the solution, implementing centrifugal clean till the pH value equals 7, and implementing centrifugally ultrasonic treatment, thereby obtain the graphene oxide quantum dot.

Abstract: A composite photocatalyst, preparation and use thereof are disclosed. The composite photocatalyst is composed of metal oxide and quantum dot material. Based on the photocatalyst, the percentage content of the metal oxide is from 80 to 99.99% by mass, and the percentage content of the quantum dot material is form 0.01 to 20% by mass. The metal oxide is zinc oxide or titanium oxide. The quantum dot material is graphene quantum dot or carbon quantum dot. The preparation is that the metal oxide and quantum dot material are stirred, mixed, ultrasonicated and dried in sequence, and the photocatalyst is obtained. Compared with other photocatalysts, the catalyst has higher catalytic efficiency and faster catalytic rate for Rhodamine B and provides more sufficient and more comprehensive utilization of sunlight.