Abstract: Disclosed are a low-shrinkage, high-strength, and large ceramic plate and a manufacturing method thereof. The method comprises the following steps: (1) preparing a ceramic raw material powder; (2) subjecting an acicular wollastonite to surface coating with a silane coupling agent and to pre-dispersion with a fumed silica to obtain a pre-treated acicular wollastonite; and (3) thoroughly mixing the ceramic raw material powder and the pre-treated acicular wollastonite and granulating the resulting mixture, the amount of the pre-treated acicular wollastonite added being 10 wt % to 30 wt % of the ceramic raw material powder, and subjecting the resulting granules to dry pressing and sintering to obtain the large ceramic plate. The acicular wollastonite is incorporated into the manufacturing of the large ceramic plate to take full advantage of the reinforcing effect and low sintering shrinkage characteristics of the acicular wollastonite. The invention reduces sintering shrinkage and increases product strength.

Abstract: Disclosed are a semi-transparent ceramic sheet decorated through ink light-absorbance and a preparation method thereof. The semi-transparent ceramic sheet comprises a semi-transparent green body, an inner inkjet pattern layer infiltrating into the semi-transparent green body from an upper surface of the semi-transparent green body, a decoloration glaze layer located on the upper surface, and a surface pattern layer located on the decoloration glaze layer. The decoloration glaze layer is capable of decoloring the ink of the inner inkjet pattern layer. The semi-transparent ceramic sheet is provided with the decoloration glaze layer so that the inkjet decoration of the inner inkjet pattern layer cannot be displayed on the surface, and the decorative pattern on the surface of the green body is the surface pattern layer and the inner inkjet pattern layer is completely in the inner layer of the green body.

Abstract: Disclosed are a low-shrinkage, high-strength, and large ceramic plate and a manufacturing method thereof. The method comprises the following steps: (1) preparing a ceramic raw material powder; (2) subjecting an acicular wollastonite to surface coating with a silane coupling agent and to pre-dispersion with a fumed silica to obtain a pre-treated acicular wollastonite; and (3) thoroughly mixing the ceramic raw material powder and the pre-treated acicular wollastonite and granulating the resulting mixture, the amount of the pre-treated acicular wollastonite added being 10 wt % to 30 wt % of the ceramic raw material powder, and subjecting the resulting granules to dry pressing and sintering to obtain the large ceramic plate. The acicular wollastonite is incorporated into the manufacturing of the large ceramic plate to take full advantage of the reinforcing effect and low sintering shrinkage characteristics of the acicular wollastonite. The invention reduces sintering shrinkage and increases product strength.

Abstract: Disclosed are a semi-transparent ceramic sheet decorated through ink light-absorbance and a preparation method thereof. The semi-transparent ceramic sheet comprises a semi-transparent green body, an inner inkjet pattern layer infiltrating into the semi-transparent green body from an upper surface of the semi-transparent green body, a decoloration glaze layer located on the upper surface, and a surface pattern layer located on the decoloration glaze layer. The decoloration glaze layer is capable of decoloring the ink of the inner inkjet pattern layer. The semi-transparent ceramic sheet is provided with the decoloration glaze layer so that the inkjet decoration of the inner inkjet pattern layer cannot be displayed on the surface, and the decorative pattern on the surface of the green body is the surface pattern layer and the inner inkjet pattern layer is completely in the inner layer of the green body.