Abstract: A porous fired granulated body is formed by consolidating numerous alumina particles to each other while letting mainly interconnected pores remain in network form across an entire cross section of a granulated body particle. The pores have an inner diameter controlled by a droplet diameter of a pore forming agent and have numerous precipitated alumina crystals formed on inner surfaces thereof. Manufacture is performed by spraying the pore forming agent (emulsion) onto a raw material to form a coating layer of the pore forming agent on a surface of the raw material particle and controlling the inner diameter of the pores. A porous fired granulated body of alumina having a high specific surface area and having higher strength for the same specific surface area can thus be provided by a simple manufacturing method.

Abstract: A porous fired granulated body is formed by consolidating numerous alumina particles to each other while letting mainly interconnected pores remain in network form across an entire cross section of a granulated body particle. The pores have an inner diameter controlled by a droplet diameter of a pore forming agent and have numerous precipitated alumina crystals formed on inner surfaces thereof. Manufacture is performed by spraying the pore forming agent (emulsion) onto a raw material to form a coating layer of the pore forming agent on a surface of the raw material particle and controlling the inner diameter of the pores. A porous fired granulated body of alumina having a high specific surface area and having higher strength for the same specific surface area can thus be provided by a simple manufacturing method.

Abstract: A porous fired granulated body is formed by consolidating numerous alumina particles to each other while letting mainly interconnected pores remain in network form across an entire cross section of a granulated body particle (11). The pores (13) have an inner diameter controlled by a droplet diameter of a pore forming agent and have numerous precipitated alumina crystals (15) formed on inner surfaces thereof. Manufacture is performed by spraying the pore forming agent (emulsion) onto a raw material to form a coating layer of the pore forming agent on a surface of the raw material particle and controlling the inner diameter of the pores. A porous fired granulated body of alumina having a high specific surface area and having higher strength for the same specific surface area can thus be provided by a simple manufacturing method.