Abstract: A method of manufacturing a molded article, which comprises: (a) a step of manufacturing the molded article by use of a laminate that has a first layer comprising polypropylene, and a second layer comprising one or more selected from the group consisting of polyethylene, polyamide, an ethylene-vinyl alcohol copolymer, and an ethylene-vinyl acetate copolymer.

Abstract: A resin sheet comprising polypropylene and one or more selected from the group consisting of a ? crystal nucleating agent and a petroleum resin, wherein the resin sheet has a crystallization speed at 130° C. of 2.5 min?1 or less and an isotactic pentad fraction of 95 mol % or more and 99 mol % or less.

Abstract: A resin sheet is manufactured by: forming a rapidly-cooled transparent polypropylene sheet by rapidly cooling a molten polypropylene resin; laminating on the rapidly-cooled transparent polypropylene sheet a resin layer of polyurethane resin, the polyurethane resin having a tensile-rupture elongation in a range from 150% to 900% and a softening point in a range from 50 degrees C. to 180 degrees C.; and laminating a print layer on the resin layer. A molded article having a non-planar molding made of the resin sheet is provided by insert molding. The molding is formed into a complicated shape where a part of the molding has: 150% or more of an elongation ratio; 0.8 or less of a film-thickness ratio (B/A) before and after the sheet is molded; and/or a surface area ratio (Y/X) before and after the sheet is molded in a range from 1.5 to 5.

Abstract: This laminate includes a thermoplastic resin layer and a protective layer, the protective layer including a welding layer, and the welding layer including a thermoplastic elastomer.

Abstract: A laminate which comprises a first resin layer and a second resin layer, and wherein: a resin constituting the first resin layer and a resin constituting the second resin layer are incompatible with each other, the first resin layer contains a polyolefin; the second resin layer contains a first thermoplastic resin and a second thermoplastic resin; and the first thermoplastic resin and the second thermoplastic resin are incompatible with each other, while having different solidification temperatures.

Abstract: Provided is a laminate containing, in the indicated order, a resin layer that contains a polyolefin, an adhesive layer, an undercoat layer, and a metal layer that contains metal or metal oxide.

Abstract: A laminate including, in the following order: a first layer formed of polypropylene containing a smectic crystal; and a second layer formed of a resin composition containing a thermoplastic resin and a metal foil powder, wherein the metal foil powder is a flattened piece having a laminate structure in which both surfaces of a metal thin film layer are each covered with a transparent thin film layer.

Abstract: A resin sheet is manufactured by: forming a rapidly-cooled transparent polypropylene sheet by rapidly cooling a molten polypropylene resin; laminating on the rapidly-cooled transparent polypropylene sheet a resin layer of polyurethane resin, the polyurethane resin having a tensile-rupture elongation in a range from 150% to 900% and a softening point in a range from 50 degrees C. to 180 degrees C.; and laminating a print layer on the resin layer. A molded article having a non-planar molding made of the resin sheet is provided by insert molding. The molding is formed into a complicated shape where a part of the molding has: 150% or more of an elongation ratio; 0.8 or less of a film-thickness ratio (B/A) before and after the sheet is molded; and/or a surface area ratio (Y/X) before and after the sheet is molded in a range from 1.5 to 5.

Abstract: A method of manufacturing a molded article, which comprises: (a) a step of manufacturing the molded article by use of a laminate that has a first layer comprising polypropylene, and a second layer comprising one or more selected from the group consisting of polyethylene, polyamide, an ethylene-vinyl alcohol copolymer, and an ethylene-vinyl acetate copolymer.

Abstract: A resin sheet is manufactured by: forming a rapidly-cooled transparent polypropylene sheet by rapidly cooling a molten polypropylene resin; laminating on the rapidly-cooled transparent polypropylene sheet a resin layer of polyurethane resin, the polyurethane resin having a tensile-rupture elongation in a range from 150% to 900% and a softening point in a range from 50 degrees C. to 180 degrees C.; and laminating a print layer on the resin layer. A molded article having a non-planar molding made of the resin sheet is provided by insert molding. The molding is formed into a complicated shape where a part of the molding has: 150% or more of an elongation ratio; 0.8 or less of a film-thickness ratio (B/A) before and after the sheet is molded; and/or a surface area ratio (Y/X) before and after the sheet is molded in a range from 1.5 to 5.

Abstract: A resin sheet is manufactured by: forming a rapidly-cooled transparent polypropylene sheet by rapidly cooling a molten polypropylene resin; laminating on the rapidly-cooled transparent polypropylene sheet a resin layer of polyurethane resin, the polyurethane resin having a tensile-rupture elongation in a range from 150% to 900% and a softening point in a range from 50 degrees C. to 180 degrees C.; and laminating a print layer on the resin layer. A molded article having a non-planar molding made of the resin sheet is provided by insert molding. The molding is formed into a complicated shape where a part of the molding has: 150% or more of an elongation ratio; 0.8 or less of a film-thickness ratio (B/A) before and after the sheet is molded; and/or a surface area ratio (Y/X) before and after the sheet is molded in a range from 1.5 to 5.

Abstract: A method of manufacturing a transparent recycled sheet using a multilayer sheet as a recycled resin, the multilayer sheet including a base layer and a surface layer being layered on each other and each including a crystalline resin, includes: melt-extruding a mixed resin into a raw sheet, the mixed resin being prepared by mixing a virgin resin including the crystalline resin, the recycled resin and a metallocene ethylene-alpha-olefin copolymer having a melt flow rate of 0.5 g/10 min to 6 g/10 min; and cooling the raw sheet.

Abstract: A transparent multilayer sheet of the embodiments includes a base layer and a surface layer laminated on at least one surface of the base layer. The base layer is formed of a resin composition that has a storage modulus being 2300 MPa or more at a temperature of 23 degrees C. and at a frequency of 1 Hz while being 150 MPa or less at a temperature of 140 degrees C. and at a frequency of 1 Hz and that has a crystallization speed of 1 min?1 or more.

Abstract: A compound of the formula, ##STR1## wherein R represents a hydrogen atom, a naphthyl, indanyl, tetrahydronaphthyl or pyridyl group, or a phenyl group which may have 1 to 3 substituents selected from the group consisting of a halogen atom, and an alkyl, alkenyl, alkoxy, alkanoyl, cyano, formyl, trifluoromethyl, phenyl, phenylalkyl, alkanoyl-amino, aminosulfonyl, carboxyl, alkoxycarbonyl, benzyloxycarbonyl, benzoylvinyl, phenylvinylcarbonyl, carboxyvinyl, and diphenyl-methyloxycarobnylvinyl group, A represents an oxygen or sulfur atom, and n represents an integer of 0 to 3, with the proviso that when n is an integer of 0, R must not be a hydrogen atom, or a pharmaceutically acceptable salt thereof is effectively useful for inhibiting a complement reaction, inflammation caused by an allergic reaction, and platelet aggregation.