Abstract: The present invention relates to heat-resistant paint which is capable of forming paint film that inhibits whitening even in high-temperature environments on the order of 350-650° C. The heat-resistant paint of the present invention contains silicone resin and/or epoxy resin as well as black pigment, wherein, said black pigment contains manganese and copper, the content of manganese in said black pigment is 25-45 mass % by MnO conversion, the content of copper in said black pigment is 5-25 mass % by CuO conversion, and the content of silicon in said black pigment is 3 mass % or less by SiO2 conversion.

Abstract: The present invention relates to heat-resistant paint which is capable of forming paint film that inhibits whitening even in high-temperature environments on the order of 350-650° C. The heat-resistant paint of the present invention contains silicone resin and/or epoxy resin as well as black pigment, wherein, said black pigment contains manganese and copper, the content of manganese in said black pigment is 25-45 mass % by MnO conversion, the content of copper in said black pigment is 5-25 mass % by CuO conversion, and the content of silicon in said black pigment is 3 mass % or less by SiO2 conversion.

Abstract: In high-tech fields such as electronics, the development of new high performance materials which differ from conventional materials has received much attention. An object of the present invention is to provide a clathrate compound which can be used as a thermoelectric material, a hard material, or a semiconductor material. Atoms of an element from group 4B of the periodic table are formed into a clathrate lattice, and a clathrate compound is then formed in which specified doping atoms are encapsulated within the clathrate lattice, and a portion of the atoms of the clathrate lattice are substituted with specified substitution atoms. Suitable doping atoms are atoms from group 1A, group 2A, group 3A, group 1B, group 2B, group 3B, group 4A, group 5A, group 6A, and group 8, and suitable substitution atoms are atoms from group 1A, group 2A, group 3A, group 1B, group 2B, group 3B, group 5A, group 6A, group 7A, group 5B, group 6B, group 7B, and group 8 of the periodic table.

Abstract: In high-tech fields such as electronics, the development of new high performance materials which differ from conventional materials has received much attention. An object of the present invention is to provide a clathrate compound which can be used as a thermoelectric material, a hard material, or a semiconductor material. Atoms of an element from group 4B of the periodic table are formed into a clathrate lattice, and a clathrate compound is then formed in which specified doping atoms are encapsulated within the clathrate lattice, and a portion of the atoms of the clathrate lattice are substituted with specified substitution atoms. Suitable doping atoms are atoms from group 1A, group 2A, group 3A, group 1B, group 2B, group 3B, group 4A, group 5A, group 6A, and group 8, and suitable substitution atoms are atoms from group 1A, group 2A, group 3A, group 1B, group 2B, group 3B, group 5A, group 6A, group 7A, group 5B, group 6B, group 7B, and group 8 of the periodic table.

Abstract: The present invention provides a clathrate compound which can be used as a thermoelectric material, a hard material, or a semiconductor material. Silicon or carbon are formed into a clathrate lattice, and a clathrate compound is then formed in which specified doping atoms are encapsulated within the clathrate lattice, and a portion of the atoms of the clathrate lattice are substituted with specified substitution atoms. The clathrate lattice is, for example, a silicon clathrate 34 (Si34) mixed lattice of a Si20 cluster including a dodecahedron of Si atoms, and a Si28 cluster including a hexahedron of Si atoms. Suitable doping atoms are atoms from group 1A, group 2A, group 3A, group 1B, group 2B, group 3B, group 4A, group 5A, group 6A, and group 8, and suitable substitution atoms are atoms from group 1A, group 2A, group 3A, group 1B, group 2B, group 3B, group 5A, group 6A, group 7A, group 5B, group 6B, group 7B, and group 8 of the periodic table.

Abstract: There is provided Ceramic matrix composites comprising fibers, BN coating applied to the fibers, the BN coating being composed of BN and one of Y.sub.2 O.sub.3, Sc.sub.2 O.sub.3, ZrO.sub.2 and lanthanoid family oxide or combinations thereof, and matrices interposed between the fibers. There is also provided Ceramic matrix composites comprising, fibers, BN coating applied to the fibers, the BN coating is composed of BN and coated with one of Y.sub.2 O.sub.3, Sc.sub.2 O.sub.3, ZrO.sub.2 and lanthanoid family oxide or combinations thereof, and matrices interposed between the fibers. The ceramic matrix composites in accordance with the present invention is capable of being used at 1000 degrees centigrade or greater in air.