Abstract: A thermal detector and method of making the same in which a suspension of binder-encapsulated copper particles is produced by comminuting a chip formed by dry-milling a major amount of copper particles with a minor amount of a binder and a charge director to produce the chip of copper particles in an encapsulant having functional sites. The bits of comminuted material are wet-milled with a major amount of a low-boiling aliphatic hydrocarbon to produce a suspension from which encapsulated copper particles are deposited on a substrate by electrophoresis. The deposit is electron-beam cured to form the detector.

Abstract: A magnetic recording medium having a coating of magnetic particles deposited thereon by electrophoresis. Magnetic particles are encapsulated by dry milling in a thermoplastic binder which is insoluble at ambient or room temperatures and is softenable at temperatures higher than 70.degree. C. A charge director for producing functional sites in the higher is incorporated in the encapsulating polymer during the dry-milling step. The encapsulated mass is comminuted or pulverized and then wet-milled with a major amount of a low-boiling aliphatic hydrocarbon liquid. A suspension is then formed with additional hydrocarbon liquid. Additional charge director may be added, either during the wet-milling step or during the suspension-forming step. The suspension is then used as a bath from which the coating is deposited by electrophoresis. The magnetic particles are oriented by the application of a magnetic field, either during the depositing step or subsequent thereto.

Abstract: A magnetic recording medium having a coating of magnetic particles deposited thereon by electrophoresis. Magnetic particles are encapsulated by dry milling in a thermoplastic binder which is insoluble at ambient or room temperatures and is softenable at temperatures higher than 70.degree. C. A charge director for producing functional sites in the binder is incorporated in the encapsulating polymer during the dry-milling step. The encapsulated mass is comminuted or pulverized and then wet-milled with a major amount of a low-boiling aliphatic hydrocarbon liquid. A suspension is then formed with additional hydrocarbon liquid. Additional charge director may be added, either during the wet-milling step or during the suspension-forming step. The suspension is then used as a bath from which the coating is deposited by electrophoresis. The magnetic particles are oriented by the application of a magnetic field, either during the depositing step or subsequent thereto.