Abstract: A molding material mixture for producing casting molds for metal processing, particularly for non-ferrous metals, such as aluminum or magnesium, is intended to reduce problems such as metal-mold reaction and/or shrinkage porosity defect. The free-flowing refractory molding material in the molding material mixture is coated with a mixture of inorganic salts exhibiting a eutectic melting point in the range of about 400 C to about 500 C, particularly in the range of about 420 C to about 460 C. Preferably this coating occurs by contacting the inorganic salt mixture with the molding material mixture at a temperature between 500 C and 700 C, in a manner that maintains the free-flowing nature of the coated product. One mixture of inorganic salts that is used is a mixture consisting of, by weight: 74% potassium fluoroborate; 15% potassium chloride; and 12% potassium fluoride. This mixture has a eutectic melting point of 420 C.

Abstract: A molding material mixture for producing casting molds for metal processing, particularly for non-ferrous metals, such as aluminum or magnesium, is intended to reduce problems such as metal-mold reaction and/or shrinkage porosity defect. The free-flowing refractory molding material in the molding material mixture is coated with a mixture of inorganic salts exhibiting a eutectic melting point in the range of about 400 C to about 500 C, particularly in the range of about 420 C to about 460 C. Preferably this coating occurs by contacting the inorganic salt mixture with the molding material mixture at a temperature between 500 C and 700 C, in a manner that maintains the free-flowing nature of the coated product. One mixture of inorganic salts that is used is a mixture consisting of, by weight: 74% potassium fluoroborate; 15% potassium chloride; and 12% potassium fluoride. This mixture has a eutectic melting point of 420 C.