Abstract: A method of manufacturing ceramic tape includes a step of directing a tape of partially-sintered ceramic into a furnace. The tape is partially-sintered such that grains of the ceramic are fused to one another yet the tape still includes at least 10% porosity by volume, where the porosity refers to volume of the tape unoccupied by the ceramic. The method further includes steps of conveying the tape through the furnace and further sintering the tape as the tape is conveyed through the furnace. The porosity of the tape decreases during the further sintering step.

Abstract: A method of manufacturing ceramic tape includes a step of directing a tape of partially-sintered ceramic into a furnace. The tape is partially-sintered such that grains of the ceramic are fused to one another yet the tape still includes at least 10% porosity by volume, where the porosity refers to volume of the tape unoccupied by the ceramic. The method further includes steps of conveying the tape through the furnace and further sintering the tape as the tape is conveyed through the furnace. The porosity of the tape decreases during the further sintering step.

Abstract: A method of manufacturing ceramic tape includes a step of directing a tape of partially-sintered ceramic into a furnace. The tape is partially-sintered such that grains of the ceramic are fused to one another yet the tape still includes at least 10% porosity by volume, where the porosity refers to volume of the tape unoccupied by the ceramic. The method further includes steps of conveying the tape through the furnace and further sintering the tape as the tape is conveyed through the furnace. The porosity of the tape decreases during the further sintering step.

Abstract: A method of manufacturing ceramic tape includes a step of directing a tape of partially-sintered ceramic into a furnace. The tape is partially-sintered such that grains of the ceramic are fused to one another yet the tape still includes at least 10% porosity by volume, where the porosity refers to volume of the tape unoccupied by the ceramic. The method further includes steps of conveying the tape through the furnace and further sintering the tape as the tape is conveyed through the furnace. The porosity of the tape decreases during the further sintering step.

Abstract: A method of manufacturing ceramic tape includes a step of directing a tape of partially-sintered ceramic into a furnace. The tape is partially-sintered such that grains of the ceramic are fused to one another yet the tape still includes at least 10% porosity by volume, where the porosity refers to volume of the tape unoccupied by the ceramic. The method further includes steps of conveying the tape through the furnace and further sintering the tape as the tape is conveyed through the furnace. The porosity of the tape decreases during the further sintering step.

Abstract: A method of manufacturing ceramic tape includes a step of directing a tape of partially-sintered ceramic into a furnace. The tape is partially-sintered such that grains of the ceramic are fused to one another yet the tape still includes at least 10% porosity by volume, where the porosity refers to volume of the tape unoccupied by the ceramic. The method further includes steps of conveying the tape through the furnace and further sintering the tape as the tape is conveyed through the furnace. The porosity of the tape decreases during the further sintering step.

Abstract: A method of manufacturing ceramic tape includes a step of directing a tape of partially-sintered ceramic into a furnace. The tape is partially-sintered such that grains of the ceramic are fused to one another yet the tape still includes at least 10% porosity by volume, where the porosity refers to volume of the tape unoccupied by the ceramic. The method further includes steps of conveying the tape through the furnace and further sintering the tape as the tape is conveyed through the furnace. The porosity of the tape decreases during the further sintering step.

Abstract: A waveguide includes a body of material having a width, a thickness, and a length, where the width is orthogonal to the thickness, and the length is orthogonal to the thickness and the width. The material includes polycrystalline ceramic that is transmissive such that the body is configured as a waveguide. The thickness is no more than 5 millimeters and at least 20 nanometers, the width is greater than or equal to the thickness, and the length is at least 100 times greater than the width. The body of material has a granular profile such that grains of the material protrude generally outward from a surface of the body with a height of at least 25 nanometers and no more than 100 micrometers relative to recessed portions of the surface of the body at boundaries between the grains.

Abstract: A waveguide includes a body of material having a width, a thickness, and a length, where the width is orthogonal to the thickness, and the length is orthogonal to the thickness and the width. The material includes polycrystalline ceramic that is transmissive such that the body is configured as a waveguide. The thickness is no more than 5 millimeters and at least 20 nanometers, the width is greater than or equal to the thickness, and the length is at least 100 times greater than the width. The body of material has a granular profile such that grains of the material protrude generally outward from a surface of the body with a height of at least 25 nanometers and no more than 100 micrometers relative to recessed portions of the surface of the body at boundaries between the grains.

Abstract: A manufacturing line includes a tape of green material that is directed through a furnace so that the furnace burns off organic binder material and then partially sinters the tape without the use of a setter board. Sintered articles resulting from the manufacturing line may be thin with relatively large surface areas; and, while substantially unpolished, have few sintering-induced surface defects. Tension may be applied to the partially sintered tape as it passes through a second furnace on the manufacturing line to shape resulting sintered articles.

Abstract: A manufacturing line includes a tape of green material that is directed through a furnace so that the furnace burns off organic binder material and then partially sinters the tape without the use of a setter board. Sintered articles resulting from the manufacturing line may be thin with relatively large surface areas; and, while substantially unpolished, have few sintering-induced surface defects. Tension may be applied to the partially sintered tape as it passes through a second furnace on the manufacturing line to shape resulting sintered articles.

Abstract: A manufacturing line includes a tape of green material that is directed through a furnace so that the furnace burns off organic binder material and then partially sinters the tape without the use of a setter board. Sintered articles resulting from the manufacturing line may be thin with relatively large surface areas; and, while substantially unpolished, have few sintering-induced surface defects. Tension may be applied to the partially sintered tape as it passes through a second furnace on the manufacturing line to shape resulting sintered articles.

Abstract: A manufacturing line includes a tape of green material that is directed through a furnace so that the furnace burns off organic binder material and then partially sinters the tape without the use of a setter board. Sintered articles resulting from the manufacturing line may be thin with relatively large surface areas; and, while substantially unpolished, have few sintering-induced surface defects. Tension may be applied to the partially sintered tape as it passes through a second furnace on the manufacturing line to shape resulting sintered articles.

Abstract: A manufacturing line includes a tape of green material that is directed through a furnace so that the furnace burns off organic binder material and then partially sinters the tape without the use of a setter board. Sintered articles resulting from the manufacturing line may be thin with relatively large surface areas; and, while substantially unpolished, have few sintering-induced surface defects. Tension may be applied to the partially sintered tape as it passes through a second furnace on the manufacturing line to shape resulting sintered articles.

Abstract: A manufacturing line includes a tape of green material that is directed through a furnace so that the furnace burns off organic binder material and then partially sinters the tape without the use of a setter board. Sintered articles resulting from the manufacturing line may be thin with relatively large surface areas; and, while substantially unpolished, have few sintering-induced surface defects. Tension may be applied to the partially sintered tape as it passes through a second furnace on the manufacturing line to shape resulting sintered articles.

Abstract: A manufacturing line includes a tape of green material that is directed through a furnace so that the furnace burns off organic binder material and then partially sinters the tape without the use of a setter board. Sintered articles resulting from the manufacturing line may be thin with relatively large surface areas; and, while substantially unpolished, have few sintering-induced surface defects. Tension may be applied to the partially sintered tape as it passes through a second furnace on the manufacturing line to shape resulting sintered articles.

Abstract: A device for testing the circuitry of a ceramic sheet-type, multi-cell solid oxide fuel cell is provided. The testing device includes a support plate having a substantially flat face, and a plurality of resilient contacts mounted on the flat face of the support plate. The contacts are spaced-apart so that each contact is individually registrable with one of the plurality of spaced-apart cells when the support plate of the device is positioned over fuel cell, allowing the circuit integrity of all of the cells to be tested simultaneously. The support plate includes a light conducting portion that visually facilitates alignment and engagement between said resilient contact members and the cells when the device is positioned over the solid oxide fuel cell. The light conducting portion of the support plate may be a transparent material that forms all or part of the plate.