Abstract: Fluorided silica-coated alumina activator-supports have a bulk density from 0.15 to 0.37 g/mL, a total pore volume from 0.85 to 2 mL/g, a BET surface area from 200 to 500 m2/g, an average pore diameter from 10 to 25 nm, and from 80 to 99% of pore volume in pores with diameters of greater than 6 nm. Methods of making the fluorided silica-coated alumina activator-supports and using the fluorided silica-coated aluminas in catalyst compositions and olefin polymerization processes also are described. Representative ethylene-based polymers produced using the compositions and processes have a melt index of 0.1 to 10 g/10 min and a density of 0.91 to 0.96 g/cm3, and contain from 70 to 270 ppm solid oxide and from 2 to 18 ppm fluorine.

Abstract: Fluorided silica-coated alumina activator-supports have a bulk density from 0.15 to g/mL, a total pore volume from 0.85 to 2 mL/g, a BET surface area from 200 to 500 m2/g, an average pore diameter from 10 to 25 nm, and from 80 to 99% of pore volume in pores with diameters of greater than 6 nm. Methods of making the fluorided silica-coated alumina activator-supports and using the fluorided silica-coated aluminas in catalyst compositions and olefin polymerization processes also are described. Representative ethylene-based polymers produced using the compositions and processes have a melt index of 0.1 to 10 g/10 min and a density of 0.91 to 0.96 g/cm3, and contain from 70 to 270 ppm solid oxide and from 2 to 18 ppm fluorine.

Abstract: A method for preparing an insensitive bis(2,2-dinitropropyl)nitramine (BDNPN) as a fine powder which exhibits desirable insensitive munitions (IM) characteristics for use alone or compounded with other energetic materials such as RDX.

Abstract: A lead-free primer energetic composition including Cyanuric Triazide (60%), Tetracene (5%), Barium Nitrate (20%) and Antimony Trisulfide (15%) is produced. The lead-free primer energetic composition is used to construct a primary detonator including a transfer charge of Cyanuric Triazide, which produces a further initiation train that may subsequently detonate a secondary explosive, i.e., HDX, RDX, or a pyrotechnic device.

Abstract: A detonator for a hand grenade fuze comprises a detonator case; a slider that is transversely reciprocable in the detonator case from an unarmed position to an armed position, the slider including a longitudinal through-hole filled with a primary explosive; a spring that biases the slider to the unarmed position; an arming mechanism attached to the slider, the arming mechanism comprising a shape memory alloy; an explosive lead disposed below the slider; and a booster charge disposed below the explosive lead.

Abstract: The invention relates to a novel polyazido compound: 2,2-dinitro-1,3-diazidopropane.

Abstract: The compound 3a,8a-bis-azidomethyl-3a,4,8a,9-tetrahydro-3H,8H-bis-[1,2,3]triazolo[1,5-a;1?,5?-d]pyrazine, whose structure is depicted below, is disclosed:

Abstract: The compound 2,2-bis(azidomethyl)oxirane, whose structure is depicted below, is disclosed:

Abstract: This invention relates to a series of novel compounds having the general structures A and B: including 2-azido-2-azidomethyl-1,3-diazidopropane (1), 2-azidomethyl-2-hydroxy-1,3-diazidopropane (2), 2-azidomethyl-2-nitrato-1,3-diazidopropane (3), 2-azidomethyl-2-nitro-1,3-diazidopropane (4), 2,2-dinitro-1,3-diazidopropane (5), methallyidiazide (6), a dimer of methallyidiazide (6), comprising 3a,8a-Bis-azidomethyl-3a,4,8a,9-tetrahydro-3H,8H-bis[1,2,3]triazolo[1,5-a;1?,5?-d]pyrazine (6-Dimer), 1,3-diazidoacetone (7), and 2-Oximido-1,3-diazidopropane (8). Also shown are reaction intermediates of these compounds, including 2,2-bis(chloromethyl)oxirane (9), and 2,2-bis(azidomethyl)oxirane (10).