Abstract: A high-strength steel product is described that includes a composition consisting of, in terms of weight percentages, 0.02% to 0.05% C, 0.1% to 0.6% Si, 1.1% to 2.0% Mn, 0.01% to 0.15% Al, 0.01% to 0.08% Nb, 0.5% or less Cu, 0.5% or less Cr, 0.7% or less Ni, 0.03% or less Ti, 0.1% or less Mo, 0.1% or less V, 0.0005% or less B, 0.015% or less P, 0.005% or less S, and the remainder being Fe and inevitable impurities, wherein the steel product has a microstructure comprising a matrix consisting of, in terms of volume percentages, 40% to 80% quasi-polygonal ferrite, 20% to 40% polygonal ferrite, 20% or less bainite, and the remainder being pearlite and martensite of 20% or less.

Abstract: Disclosed is a high-strength steel product comprising a composition consisting of, in terms of weight percentages, 0.02% to 0.05% C, 0.1% to 0.6% Si, 1.1% to 2.0% Mn, 0.01% to 0.15% Al, 0.01% to 0.08% Nb, 0.5% or less Cu, 0.5% or less Cr, 0.7% or less Ni, 0.03% or less Ti, 0.1% or less Mo, 0.1% or less V, 0.0005% or less B, 0.015% or less P, 0.005% or less S, and the remainder being Fe and inevitable impurities, wherein the steel product has a microstructure comprising a matrix consisting of, in terms of volume percentages, 40% to 80% quasi-polygonal ferrite, 20% to 40% polygonal ferrite, 20% or less bainite, and the remainder being pearlite and martensite of 20% or less. The steel product has a yield strength of at least 400 MPa, an ultimate tensile strength of at least 500 MPa, and a Charpy-V impact toughness of at least 34 J/cm2 at a temperature in the range of ?50° C. to ?100° C.

Abstract: The present invention relates to thin hot-rolled ultrahigh strength steel (UHSS) products, i.e. to hot-rolled steel strips with ultrahigh strength and good bendability. The object of the present invention is to provide an ultrahigh strength hot-rolled steel product that is having yield strength Rp0.2 at least 840 MPa and improved bendability. Further, a preferred aim is also to achieve an ultrahigh strength steel strip with excellent low temperature impact toughness. The inventors of the present invention have surprisingly found that the bendability of directly quenched ultrahigh strength steel strip can be significantly improved by producing a microstructure comprising upper bainite as main phase and by having a hot-rolled steel strip product having a yield strength Rp0.2 at least 840 MPa and a thickness of less than 12 mm, whose composition in percentage by weight is C: 0.03-0.08, Si: 0.01-0.8, Mn: 0.8-2.5, Al: 0.01-0.15, Cr: 0.01-2.0, B: 0.0005-0.005 Nb: 0.005-0.07, Ti: 0.005-0.12, N:<0.01, P:<0.

Abstract: The present invention relates to thin hot-rolled ultrahigh strength steel (UHSS) products, i.e. to hot-rolled steel strips with ultrahigh strength and good bendability. The object of the present invention is to provide an ultrahigh strength hot-rolled steel product that is having yield strength Rp0.2 at least 840 MPa and improved bendability. Further, a preferred aim is also to achieve an ultrahigh strength steel strip with excellent low temperature impact toughness. The inventors of the present invention have surprisingly found that the bendability of directly quenched ultrahigh strength steel strip can be significantly improved by producing a microstructure comprising upper bainite as main phase and by having a hot-rolled steel strip product having a yield strength Rp0.2 at least 840 MPa and a thickness of less than 12 mm, whose composition in percentage by weight is C: 0.03-0.08, Si: 0.01-0.8, Mn: 0.8-2.5, Al: 0.01-0.15, Cr: 0.01-2.0, B: 0.0005-0.005 Nb: 0.005-0.07, Ti: 0.005-0.12, N:<0.01, P:<0.