Abstract: The present invention relates to a new process for improving dewatering when manufacturing a film comprising high amounts of microfibrillated cellulose (MFC) without negatively impacting the film properties. According to the present invention a high amount of nanoparticles is used as an additive, optionally together with a polymer.

Abstract: The present invention relates to a method for preparing a surface-treated fibrous material comprising nanocellulose, in which a fibrous material is surface treated with an organic acid or salt thereof. Fibrous materials as such are also provided. The present technology allows improved Water Vapor Transmission Rates (WVTR) for the fibrous material, while operating on an industrial scale.

Abstract: The present invention relates to a method for preparing a surface-treated fibrous material comprising phosphorylated nanocellulose, in which a fibrous material is surface treated with a solution comprising at least one multivalent metal ion followed by drying and post-curing to improve the barrier properties of the material. Fibrous materials as such are also provided.

Abstract: A method for the production of a fibrous product from a fibrous web, wherein the method comprises the steps of: —providing a fibrous suspension comprising a microfibrillated cellulose, wherein the content of the microfibrillated cellulose of said suspension is in the range of 60 to 99.9 weight-% based on total dry solid content, —adding an uncharged, amphoteric or weakly cationic polymer having a molecular weight of at least 50000 g/mol to said suspension, —adding an anionic polymer having a molecular weight of at least 00000 g/mol to said suspension to provide a mixture of said microfibrillated cellulose, said uncharged, amphoteric or weakly cationic polymer and said anionic polymer, 1—providing said mixture to a substrate to form a fibrous web, wherein the amount of uncharged, amphoteric or weakly cationic polymer in said mixture is in the range of 0.1 to 20 kg/metric ton based on total dry solid content and wherein the amount of anionic polymer in said mixture is in the range of 0.

Abstract: The present invention relates to an UV blocking film comprising microfibrillated cellulose wherein at least part of the microfibrillated cellulose is microfibrillated cellulose produced from non-chemical modified lignocellulosic material. The invention also relates to a method for producing the film, use of said film as well as a composition having UV blocking properties.

Abstract: The present invention relates to a method for manufacturing a film comprising microfibrillated cellulose wherein the method comprises the steps of; providing a suspension comprising a microfibrillated cellulose, adding an enzyme to the suspension, mixing the enzyme with the suspension to form a mixture, applying said mixture to a wire to form a fibrous web and drying said web to form said film. The present invention further relates to a film comprising microfibrillated cellulose having good barrier properties.

Abstract: A method of manufacturing a film having an oxygen transmission rate (OTR) value in the range of 0.1 to 200 cc/m2*24 h at 23° C., 50% relative humidity (RH), and an OTR value in the range of 0.1 to 2000 cc/m2*24 h at 38° C. at 85% RH, comprising at least 60% by weight nanocellulose based on the weight of the total amount of fibers in the film, wherein the method comprises the steps of, providing an aqueous suspension comprising said nanocellulose; forming a web from said aqueous suspension; calendering said web at a line load of at least 40 kN/m, and at a temperature of at least 60° C. wherein said film is formed and said web has an OTR value in the range of 50 to 10 000 cc/m2*24 h at 23° C., 50% RH before said calendering step, or more preferably in the range of 500 to 5000 cc/m2*24 h at 23° C., 50% RH before said calendering step.

Abstract: The present invention relates to a method for manufacturing an intermediate product that can be stored and transported and efficiently converted into microfibrillated cellulose with limited energy input at the time of conversion. More specifically, the invention involves the use of dewatered carboxymethylcellulose or carboxylated cellulose fiber having a low degree of substitution and a high amount of additives.

Abstract: The present invention relates to an UV blocking film comprising microfibrillated cellulose wherein at least part of the microfibrillated cellulose is microfibrillated cellulose produced from non-chemical modified lignocellulosic material. The invention also relates to a method for producing the film, use of said film as well as a composition having UV blocking properties.

Abstract: Method for making a film that comprises microfibrillated cellulose, wherein the film has low OTR values and especially suitable for a tropical environment. The method comprising the steps of providing a suspension comprising microfibrillated cellulose (MFC), forming a film from said suspension, wherein the film having a solid content above 40%, preferably above 50%, treating the film with flame or plasma treatment, such that a surface activation takes place on the film, and cooling the film, wherein the surface of the film having a decreased OTR value and a high moisture resistance.

Abstract: The present invention relates to a new process for improving dewatering when manufacturing a film comprising high amounts of microfibrillated cellulose (MFC) without negatively impacting the film properties. According to the present invention a high amount of nanoparticles is used as an additive, optionally together with a polymer.