Abstract: Provided is a beta zeolite satisfying P>76.79Q?29.514 in a range in which Q is less than 0.4011 nm, wherein, P represents an AB value that is an intensity ratio of A to B, A represents a diffraction intensity of a main peak of the beta zeolite observed by X-ray diffraction measurement, B represents a diffraction intensity of the (116) plane of ?-alumina obtained by X-ray diffraction measurement under the same conditions as those for the X-ray diffraction measurement on the beta zeolite, the ?-alumina being the standard substance 674a distributed by the American National Institute of Standards and Technology, and Q represents a lattice interplanar spacing of the main peak of the beta zeolite observed by X-ray diffraction measurement. It is preferable that the formula (1) above is satisfied in a range in which Q is from 0.3940 to 0.4000 nm.

Abstract: An aerated composite material produced from carbonatable calcium silicate compositions (carbonation cured AAC) that has a compressive strength equivalent to autoclaved aerated concrete (ordinary AAC) at substantially the same density and a process of production of the same are provided. The composite material of the present invention comprises: a plurality of bonding elements, each including a core comprising calcium silicate, a first layer which partially or fully surrounds the core and is rich in SiO2, and a second layer which partially or fully surrounds the first layer and is rich in CaCO3; a plurality of filler particles having their particle sizes ranging from 0.1 ?m to 1000 ?m; and a plurality of voids; wherein the plurality of bonding elements and plurality of filler particles together form a bonding matrix and are substantially evenly dispersed in the matrix and bonded together, the plurality of voids are bubble-shaped and/or interconnected channels, a pore volume with a radius of 0.004 ?m to 10.

Abstract: An aerated composite material produced from carbonatable calcium silicate compositions (carbonation cured AAC) that has a compressive strength equivalent to autoclaved aerated concrete (ordinary AAC) at substantially the same density and a process of production of the same are provided. The composite material of the present invention comprises: a plurality of bonding elements, each including a core comprising calcium silicate, a first layer which partially or fully surrounds the core and is rich in SiO2, and a second layer which partially or fully surrounds the first layer and is rich in CaCO3; a plurality of filler particles having their particle sizes ranging from 0.1 ?m to 1000 ?m; and a plurality of voids; wherein the plurality of bonding elements and plurality of filler particles together form a bonding matrix and are substantially evenly dispersed in the matrix and bonded together, the plurality of voids are bubble-shaped and/or interconnected channels, a pore volume with a radius of 0.004 ?m to 10.