Abstract: Stainless steel is improved in anti-microbial property by the addition of Cu in an amount of 0.4-5.0 wt. % and the precipitation of Cu-rich phase at the ratio of 0.2 vol. % or more. The Cu-rich phase is precipitated as minute particles uniformly dispersed in the matrix not only at the surface layer but also at the interior by heat treatment such as annealing or aging at 500.degree.-900.degree.. Since the anti-microbial property is derived from the material itself, the underlying stainless steel does not lose the excellent anti-microbial property even after it is polished or mechanically worked. Due to the anti-microbial property, the stainless steel is useful as material in various fields requiring sanitary environments, for example, kitchen goods, electric home appliances, devices or tools at hospitals, parts or interiors for building and grips or poles for electric trains or buses.

Abstract: A high strength and elongation stainless steel with a hardness of at least HV is formed of a duplex structure comprising 20% to 95% by volume of martensite having an average grain diameter of not more than 10 .mu.m, with the balance being essentially ferrite, the steel including, by weight, up to 0.10% C, up to 2.0% Si, up to 4.0% Mn, up to 0.040% P, up to 0.010% S, up to 4.0% Ni, from 10.0% to 20.0% Cr, up to 0.12% N, more than 0.0050% to 0.0300% B, up to 0.02% O and up to 4.0% Cu, and optionally contains up to 0.20% A1, up to 3% Mo, up to 0.20% REM, up to 0.20% Y, up to 0.10% Ca, and up to 0.10% Mg, with the balance being Fe and unavoidable impurities.

Abstract: For a purpose of providing a high strength and toughness stainless steel strip having not only a high strength of at least 1800 N/mm.sup.2 but also a high Erichsen break stress, which is a measure of toughness of a thin sheet, of as high as at least 1000 N/mm.sup.2, there is provided a stainless steel strip consists essentially of in mass % C: up to 0.1%, (exclusive of 0%); Si more than 1.0% and not more than 4.0%; Mn: up to 5.0% (exclusive of 0%); Ni: from 4.0 to 10.0%; Cr :from 12.0 to 18.0%; Cu :up to 5.0% (inclusive of 0%); Mo: from 1.0 to 5.0%; N: up to (exclusive of 0%); the balance being Fe and impurities with the proviso of C+N.gtoreq.0.1%, and wherein the alloying elements are adjusted so that a value of Md(N) defined by the following equation:Md(N)=580-520.times.[% C]-2.times.[% Si]-16.times.[% Mn]-16.times.[% Cr]-23.times.[% Ni]-26.times.[% Cu]-10.times.

Abstract: A multifold pipe made by multiple rolling up and turning of a copper coated steel sheet into a multifold pipe, characterized in that said steel sheet is a cold rolled sheet of a super soft austenitic stainless steel comprising by weight: up to 0.05% of C, up to 1.0% of Si, up to 5.0% of Mn, from 9.0% to 15.0% of Ni, from 15.0% to 20.0% of Cr, up to 0.04% of N, up to 5.0% of Cu, the balance being Fe and unavoidable impurities, wherein the alloying elements are further adjusted so that both the two relations (1) and (2) noted below are satisfied:K=20.5+13.0.times.C+0.99.times.Si-1.1.times.Mn-Ni-0.4.times.Cu +0.4.times.Cr+117.1.times.N.ltoreq.19.5 (1)H=27.1+60.9.times.C+0.26.times.Si-Ni-0.79.times.Cu+0.68 .times.Cr+52.6.times.N.ltoreq.29.0 (2)The multifold pipe according to the invention is excellent in fluid tightness of its fused part and in corrosion resistance.

Abstract: A ferric stainless steel consists by weight of less than 0.03% carbon, less than 1% silicon, less than 1% manganese, less than 0.04% phosphorus, less than 0.03% sulphur, from 15% to 25% chromium, less than 0.03% nitrogen, from 3% to 6% aluminum, from 0.1% to 4% molybdenum. A small amount of rare-earth elements and yttrium of from 0.01% to 0.15% are added in the steel.

Abstract: A high strength chromium containing steel sheet having a tensile strength of at least 40 kgf/mm.sup.2, and excellent in corrosion resistance and workability, comprising, by weight, C:up to 0.030%, Si:up to 2.30%, Mn:up to 3.0%, P:more than 0.0005% and not more than 0.150%, S:up to 0.010%, Ni:up to 2.0%, Cu:more than 0% and not more than 2.0%, Cr:not less than 5.0% and less than 10.0%, N:up to 0.030%, V:not less than 0.01% and not more than 0.10%, and optionally at least one of 0.01 to 0.30% of Ti, 0.01 to 0.30% of Nb, 0.01 to 0.30% of Zr, 0.01 to 0.20% of Al and 0.0002 to 0.0200% of B, the amounts of Si, Mn, P, Ni and Cu being adjusted so that the relation:Si+Mn+10P+Ni+Cu>1.0% may be satisfied, the balance being iron and unavoidable impurities.

Abstract: A ferric stainless steel consists by weight of less than 0.03% carbon, less than 1% silicon, less than 1% manganese, less than 0.04% phosphorus, less than 0.03% sulphur, from 15% to 25% chromium, less than 0.03% nitrogen, from 3% to 6% aluminum, from 0.1% to 4% molybdenum. A small amount of rare-earth elements and yttrium of from 0.01% to 0.15% are added in the steel.

Abstract: A chromium containing steel sheet excellent in corrosion resistance and workability, comprising, by weight, C:up to 0.030%, Si:up to 0.5%, Mn:up to 0.5%, P:up to 0.040%, S:up to 0.010%, Ni:up to 0.3%, Cu:up to 0.3%, Cr: not less than 5.0% and less than 11.0%, N:up to 0.030%, V:not less than 0.01% and not more than 0.10%, and optionally at least one of 0.01 to 0.30% of Ti, 0.01 to 0.30% of Nb, 0.01 to 0.30% of Zr, 0.01 to 0.20% of Al and 0.0002 to 0.0200% of B, the amounts of Si, Mn, P, Ni and Cu being adjusted so that the relation:Si+Mn+10P+Ni+Cu.ltoreq.1.0% may be satisfied, the balance being iron and unavoidable impurities.

Abstract: A process for the production of a stainless steel strip having excellent spring characteristics as such and good formability, wherein a cold rolled strip of a stainless steel comprising, in addition to Fe, from 10.0 to 20.0% by weight of Cr, from 0.01 to 0.15% by weight of C, and at least one of Ni, Mn and Cu in an amount of from 0.1 to 4.0% by weight, is continuously passed through a continuous heat treatment furnace where it is heated to a temperature range for a two-phase of ferrite and austenite, rapidly cooled to provide a strip of a duplex structure, consisting essentially of ferrite and martensite, optionally temper rolled at a rolling reduction of not more than 10%, and continuously passed through a continuous heat treatment furnace to effect aging of not longer than 10 minutes.

Abstract: Process for producing steel strip of duplex structure wherein cold rolled strip of chromium stainless steel comprising, in addition to Fe, 10.0% to 20.0% of Cr, to 0.10% C, to 0.12% of N, the (C+N) being 0.01% to 0.20%, to 2.0% of Si, to 4.0% of Mn to 4.0% of Ni and to 4.0% of Cu, the {Ni+(Mn+Cu)/3} being not less than 0.5% but not more than 5.0%, is continuously passed through a heating zone where it is heated to form a two-phase of ferrite and austenite and the heated strip is cooled at a cooling rate sufficient to transform the austenite to martensite. The product has high strength and elongation reduced plane anisotropy and hardness of at least HV 200.

Abstract: Ferritic stainless steel consisting essentially of, in % by weight, 0.0050 to 0.0500 of C, 10.00 to 18.00 of Cr, up to 0.50 of Si, up to 0.50 of Mn, more than 0.040 but not more than 0.200 of P, up to 0.030 of S, up to 0.60 of Ni, 0.005 to 0.200 of Sol. Al, and 0.0020 to 0.0050 of B, the balance being Fe and impurities, and having a longitudinal cracking transition temperature of not higher than -10.degree. C. as determined by the cup expansion test hereinbefore described. The steel has excellent formability and secondary workability.

Abstract: Process for producing steel strip of duplex structure wherein cold rolled strip of chromiun stainless steel comprising, in addition to Fe, 10.0% to 20.0% of Cr, to 0.15% of C, to 0.12% of N, the (C+N) being 0.02% to 0.20%, to 2.0% of Si, to 1.0% of Mn and to 0.6% of Ni, is continuously passed through a heating zone where it is heated to form a two-phase of ferrite and austenite and the heated strip is cooled at a cooling rate sufficient to transform the austenite to martensite. The product has high strength and elongation reduced plane anisotropy and hardness of at least HV 200.

Abstract: A corrosion resistant alloy comprising in % by weight up to 0.05% of C, 10.00 to 18.00% of Cr, up to 1.00% of Si, up to 1.00% of Mn, more than 0.040% but not more than 0.150% of P, up to 0.050% of S, up to 0.60% of Ni and 0.005 to 0.50% of sol.Al, the balance being Fe and unavoidable impurities. The alloy has an enhanced pickling performance of the hot rolled material and an improved workability of the cold rolled material.

Abstract: A process for the production of a strip of a corrosion resistant alloy steel having excellent workability, which process comprises subjecting a cold rolled strip of a steel containing in % by weight as essential components up to 0.05% of C, 10.00 to 18.00% of Cr, 0.005 to 0.50% of sol. Al and more than 0.040% but not more than 0.150% of P to a final annealing, said final annealing being carried out by heating the cold rolled strip in a box annealing furnace to an annealing temperature within the range between 650.degree. C. and 900.degree. C., and maintaining the strip in the furnace at the annealing temperature, the rate of heating at which the strip is heated from 300.degree. C. to the annealing temperature being not faster than 300.degree. C./hr.

Abstract: A corrosion resistant alloy comprising in % by weight up to 0.05% of C, 10.00 to 18.00% of Cr, up to 1.00% of Si, up to 1.00% of Mn, more than 0.040% but not more than 0.150% of P, up to 0.050% of S, up to 0.60% of Ni and 0.005 to 0.50% of sol.Al, the balance being Fe and unavoidable impurities. The alloy has an enhanced pickling performance of the hot rolled material and an improved workability of the cold rolled material.