Abstract: A nitrocarburized microalloyed steel member consists of a microalloyed steel that includes a nitrocarburized layer on a surface, a cross-sectional structure of which steel except for the nitrocarburized layer includes a ferrite and pearlite structure. The microalloyed steel mainly consists of Fe and has a composition: C having a content of 0.30 mass % or more and 0.50 mass % or less; Si having a content of 0.05 mass % or more and 0.30 mass % or less; Mn having a content of 0.50 mass % or more and 1.00 mass % or less; S having a content of 0.03 mass % or more and 0.20 mass % or less; Cu having a content of 0.05 mass % or more and 0.60 mass % or less; Ni having a content of 0.02 mass % or more and 1.00 mass % or less; and Cr having a content of 0.05 mass % or more and 0.30 mass % or less. If the contents of the Cu, the Ni, and the Cr are represented by WCu, WNi, and WCr mass %, respectively, and composition parameters F1 and F2 are 185WCr+50WCu and 8+4WNi+1.

Abstract: The present invention provides a coating material for forming a coating layer that can achieve excellent adhesion to a transparent film. The coating material is prepared so that it contains a thermosetting resin, an inorganic filler, and a mixed solvent containing cyclohexanone. The content of the thermosetting resin is in the range from 5 to 20 wt % with respect to the total amount of the thermosetting resin and the inorganic filler, and the content of the cyclohexanone is in the range from 25 to 35 wt % with respect to the entire mixed solvent. By coating a surface of a transparent film with this coating material and then heat-treating the resultant coating, a coating layer with excellent adhesion can be formed on transparent film. The thus-obtained laminate of the transparent film and the coating layer can be used as an antireflection film.

Abstract: A surface of a steel, as a material for a crankshaft, is nitrocarburized. The steel contains, as alloy elements C having a content 0.10 mass % or more 0.30 mass % or less, Si having a content 0.5 mass % or more and 0.3 mass % or less, Mn having a content 0.3 mass % or more and 1.5 mass % or less, Mo having a content 0.8 mass % or more and 2.0 mass % or less, Cr having a content 0.1 mass % or more and 1.0 mass % or less, and V having a content 0.1 mass % or more and 0.5 mass % or less, with a remainder consisting of Fe and inevitable impurities. The contents of the alloy elements fall within ranges: 2.0 mass %?Mn+Cr+Mo?3.0 mass %, 2.3 mass %?C+Mo+5V ?3.7 mass %, and 2.7 mass %?2.16 Cr+Mo+2.54V?4.0 mass %. If a steel sample extracted from a central portion of the nitrocarburized steel free from an influence of the nitrocarburizing treatment is austenitized at 1200° C.

Abstract: There are provided a hard-coated antiglare film with high hardness, high scratch resistance and good antiglare properties, a method of manufacturing the film, an optical element using the film, and an image display including the film or the optical element. The hard-coated antiglare film of the invention includes a transparent film substrate and a hard-coating layer that contains fine particles and is formed on at least one side of the transparent film substrate, wherein the hard-coating layer has a thickness of 15 ?m to 30 ?m, the fine particles have an average particle size of 30% to 75% of the thickness of the hard-coating layer, and the fine particles form unevenness with a ?a value of 0.4° to 1.5° according to JIS B 0601.

Abstract: The invention is directed to a hard-coated film, comprising: a transparent film substrate; and a hard-coating layer formed on at least one side of the transparent film substrate, wherein the hard-coating layer is made from a material containing a urethane acrylate, a polyol (meth)acrylate and a (meth)acrylic polymer having an alkyl group containing at least two hydroxyl groups. There can be provided a hard-coated film that has high hardness and good flexibility and is resistant to curling due to hardening and shrinking and a method of manufacturing a hard-coated film in which a reduction in production efficiency associated with an increase in the number of manufacturing steps is prevented.

Abstract: A steel for use in high strength pinion shaft which is not refined and used by applying high frequency hardening with less occurrence of peeling during hobbing, having high surface hardness, impact value and torsional strength after high frequency hardening, and with less heat treatment strains during high frequency hardening, containing, on the mass % basis; C; 0.45-0.55%, Si: 0.10-0.50%, MA: 0.50-1.20%, P: 0.025% or less, S: 0.025% or less, Mo: 0.15-0.25%, B: 0.0005-0.005%, Ti: 0.005-0.10%, and N: 0.015% or less, satisfying; 0.80≦Ceq 0.95 and f value≦1.0, and the balance of Fe and inevitable impurities, as well as a manufacturing method thereof.

Abstract: A case hardening steel which consists essentially of 0.03-0.2 wt % of C, 1.0-3.0 wt % of Si, 0.2-2.0 wt % of Mn, 0.05-0.5 wt % of V and the balance of Fe. The primary advantage of this steel is fineness of grain size after carburizing at relatively high temperatures. Even when carburizeed at or above 950.degree. C., the grain size number is not smaller than 6 in both the hardened case and the core. Optionally the steel may contain up to 2.0 wt % of Ni, up to 2.0 wt % of Cr and/or up to 0.5 wt % of Mo for the reinforcing purpose, and/or up to 0.1 wt % of Al, up to 0.3 wt % of Ti, up to 0.1 wt % of Zr, up to 0.03 wt % of N and/or up to 0.5 wt % of Nb+Ta for the purpose of depressing the grain growth.