Abstract: A process for producing a Co-base alloy which has a basic composition including, in terms of mass proportion, 0.1%-10% Al, 3.0-45% W, and Co as the remainder and has an intermetallic compound of the L12 type [Co3 (Al,W)] dispersed and precipitated therein. Part of the Co may be replaced with Ni, Ir, Fe, Cr, Re, or Ru, while part of the Al and W may be replaced with Ni, Ti, Nb, Zr, V, Ta or Hf. The intermetallic compound [Co3 (Al, W)] has a high melting point, and this compound and the matrix are mismatched little with respect to lattice constant. Thus, the cobalt-base alloy can have high-temperature strength equal to that of nickel-base alloys and excellent structure stability.

Abstract: A process for producing a Co-base alloy which has a basic composition including, in terms of mass proportion, 0.1%-10% Al, 3.0-45% W, and Co as the remainder and has an intermetallic compound of the L12 type [Co3 (Al, W)] dispersed and precipitated therein. Part of the Co may be replaced with Ni, Ir, Fe, Cr, Re, or Ru, while part of the Al and W may be replaced with Ni, Ti, Nb, Zr, V, Ta or Hf. The intermetallic compound [Co3 (Al, W)] has a high melting point, and this compound and the matrix are mismatched little with respect to lattice constant. Thus, the cobalt-base alloy can have high-temperature strength equal to that of nickel-base alloys and excellent structure stability.

Abstract: A Co-base alloy which has a basic composition including, in terms of mass proportion, 0.1%-10% Al, 3.0-45% W, and Co as the remainder and has an intermetallic compound of the Ll2 type [Co3(Al,W)] dispersed and precipitated therein. Part of the Co may be replaced with Ni, Ir, Fe, Cr, Re, or Ru, while part of the Al and W may be replaced with Ni, Ti, Nb, Zr, V, Ta or Hf. The intermetallic compound [Co3(Al, W)] has a high melting point, and this compound and the matrix are mismatched little with respect to lattice constant. Thus, the cobalt-base alloy can have high-temperature strength equal to that of nickel-base alloys and excellent structure stability.

Abstract: It is an object of the present invention to provide a ferromagnetic Fe-based alloy having a large reversible strain obtained by application and removal of a magnetic field gradient. The Fe-based alloy contains one or two or more types selected from Al: 0.01 to 11%, Si: 0.01 to 7% and Cr: 0.01 to 26%, or Al: 0.01 to 11%, Si: 0.01 to 7%, Cr: 0.01 to 26% and Ni: 35 to 50%. A twin crystal interface is introduced by working the Fe-based alloy at a working rate: 10% or more. An area ratio of the twin crystal interface to a crystal grain boundary is 0.2 or more. One or two or more types of Ti: 0.01 to 5%, V: 0.01 to 10%, Mn: 0.01 to 5%, Co: 0.01 to 30%, Ni: 0.01 to 10%, Cu: 0.01 to 5%, Zr: 0.01 to 5%, Nb: 0.01 to 5%, Mo: 0.01 to 5%, Hf: 0.01 to 5%, Ta: 0.01 to 5%, W: 0.01 to 5%, B: 0.001 to 1%, C: 0.001 to 1%, P: 0.001 to 1% and S: 0.001 to 1% may be added to the Fe-based alloy if needed.

Abstract: A Co-base alloy which has a basic composition including, in terms of mass proportion, 0.1%-10% Al, 3.0-45% W, and Co as the remainder and has an intermetallic compound of the Ll2 type [Co3(Al,W)] dispersed and precipitated therein. Part of the Co may be replaced with Ni, Ir, Fe, Cr, Re, or Ru, while part of the Al and W may be replaced with Ni, Ti, Nb, Zr, V, Ta or Hf. The intermetallic compound [Co3(Al, W)] has a high melting point, and this compound and the matrix are mismatched little with respect to lattice constant. Thus, the cobalt-base alloy can have high-temperature strength equal to that of nickel-base alloys and excellent structure stability.