Abstract: A cold-rolled steel sheet with excellent bending workability has a component composition of 0.025% or less C, 0.1% or less Si, 0.05% to 0.5% Mn, 0.03% or less P, 0.02% or less S, and 0.01% to 0.1% sol. Al on a mass basis, the remainder being Fe and unavoidable impurities; a microstructure that is a ferrite rolling texture; a tensile strength TS of 390 MPa or more; a thickness of 0.4 mm or more; and a sheet thickness direction ultimate ductility of 1.3 or more, wherein the sheet thickness direction ultimate ductility is the natural logarithm Ln(t0/t1) of the ratio of the thickness t0 of an untested steel sheet to the thickness t1 of the fracture surface of the tested steel sheet as determined by a tensile test.

Abstract: A cold-rolled steel sheet includes, on a percent by mass basis: C: 0.0010% to 0.0030%, Si: 0.05% or less, Mn: 0.1% to 0.3%, P: 0.05% or less, S: 0.02% or less, Al: 0.02% to 0.10%, N: 0.005% or less, and Nb: 0.010% to 0.030% and the remainder composed of Fe and incidental impurities, wherein r values in a rolling direction and a direction perpendicular to the rolling direction are within a range of 1.0 to 1.6, and a mean value Elm of elongations in the rolling direction, a direction at 45° with respect to the rolling direction, and the direction perpendicular to the rolling direction is 40% or more, where Elm=(ElL+2×ElD+ElC)/4 ElL: elongation in the rolling direction, ElD: elongation in the direction at 45° with respect to the rolling direction, and ElC: elongation in the direction perpendicular to the rolling direction.

Abstract: The invention proposes a high-strength dual-phase cold rolled steel sheet having an excellent deep drawability, wherein the steel sheet has a composition comprising C: 0.01-0.08 mass %, Si: not more than 2.0 mass %, Mn: not more than 3.0 mass %, P: not more than 0.10 mass %, S: not more than 0.02 mass %, A1: 0.005-0.20 mass %, N: not more than 0.02 mass % and V: 0.01-0.5 mass %, provided that V and C satisfy a relationship of 0.5×C/12≦V/51≦3×C/12, and the remainder being Fe and inevitable impurities, and has a microstructure consisting of a ferrite phase as a primary phase and a secondary phase including martensite phase at an area ratio of not less than 1% to a whole of the microstructure and a high-strength dual-phase galvanized steel sheet comprising a galvanized coating on the above steel sheet as well as a method of producing the same.

Abstract: Process and apparatus for refining silicon by treatment in a graphite vessel with irradiation with an electron beam while removing impurity elements by evaporation. A single graphite vessel is used, or plural graphite vessels are arranged in sequence. During treatment in successive graphite vessels, molten silicon is poured in succession from one vessel to another. Use of graphite vessels improves heat efficiency, prevents contamination and produces refined silicon containing very low contents of impurities.

Abstract: Method for producing highly purified silicon for use in solar cells by a single solidification purification, pouring silicon into a mold and gradually fractionally solidifying it while solidifying the liquid surface, followed by purifying the solidified silicon by zone melting or continuous casting using an electromagnetic mold, or by zone melting in combination with continuous casting, and optionally causing directional solidification to concentrate impurities, leaching and recycling.

Abstract: An object of the present invention is to provide a process and apparatus for the continuous flow production of polycrystalline silicon from metallic silicon or silicon oxide as a raw material and also for the manufacture of a wafer by using it, which process and apparatus permit the mass production at a low cost.