Abstract: This invention relates to a process for manufacturing a spray urethane elastomer. More particularly it relates to a process for manufacturing a solventless, non-cellular spray urethane elastomer, which comprises spraying a partial prepolymer component having a high molar ratio of NCO/OH prepared from an organic polyisocyanate and from polytetramethylene ether glycol (PTMEG) having a molecular weight of 400 to 2000 and a resin component containing the PTMEG, a specified chain extender and an organobismuth compound catalyst onto a substrate by use of a two components high pressure spray machine.According to the present invention, spraying only of the stock solutions by use of the two components high pressure spray machine accomplishes coating and the stock solutions are cured in one second to ten and several seconds after being sprayed without producing cells even when thick-coated.

Abstract: Disclosed is a process for preparing fine needle-like, ferromagnetic iron compound particles for use in magnetic recording in which needle-like iron oxyhydroxide fine particles prepared by simultaneously co-precipitating or cladding iron compound particles with an element of group II of the Periodic Table and manganese at atomic weight ratios of the element of group II of the Periodic Table and manganese to iron of from 0.001/100 to 10/100 and 0.005/100 to 10/100 respectively are reduced and/or oxidized under heating.