Abstract: To provide a sliding member that improves seizure resistance by restraining any exposure of the porous layer and improves abrasion resistance and load resistance. The sliding member 1 constitutes a bearing having a cylindrical shape, an inner circumferential surface of which is a sliding layer 5 with an axis. In the sliding member 1, a porous layer 3 made of alloy material is formed on a surface of a metal base 2 and this porous layer 3 is covered by resin material 4 so that the sliding layer 5 is formed. In the sliding member 1, a particle size of metal powder 30 forming the porous layer 3 is within a range of 15 through 60 ?m, preferably, about 25 through 45 ?m. Further, in the sliding member 1, a thickness of the porous layer 3 is within a range of 0.06 through 0.1 mm and a thickness of the sliding layer 5 is within a range of 0.08 through 0.16 mm The thickness of the sliding layer 5 is set to be thicker on average than the thickness of the porous layer 3 so that the porous layer 3 is not exposed.

Abstract: To provide a sliding member that improves seizure resistance by restraining any exposure of the porous layer and improves abrasion resistance and load resistance. The sliding member 1 constitutes a bearing having a cylindrical shape, an inner circumferential surface of which is a sliding layer 5 with an axis. In the sliding member 1, a porous layer 3 made of alloy material is formed on a surface of a metal base 2 and this porous layer 3 is covered by resin material 4 so that the sliding layer 5 is formed. In the sliding member 1, a particle size of metal powder 30 forming the porous layer 3 is within a range of 15 through 60 ?m, preferably, about 25 through 45 ?m. Further, in the sliding member 1, a thickness of the porous layer 3 is within a range of 0.06 through 0.1 mm and a thickness of the sliding layer 5 is within a range of 0.08 through 0.16 mm The thickness of the sliding layer 5 is set to be thicker on average than the thickness of the porous layer 3 so that the porous layer 3 is not exposed.

Abstract: In the field of biocompatible Co—Cr—Mo alloys for use in artificial joints or the like, the formation of wear debris in a living body is a matter of concern. The purpose of the invention is to provide a technique for improving the wear resistance of a Co—Cr—Mo alloy for use in an artificial joint to thereby prevent the formation of wear debris in a living body. The improvement in wear resistance of a Co—Cr—Mo alloy for use in an artificial joint can be achieved by finely dividing the crystal particles of the alloy, by preparing an alloy composition having a higher Mo content than any known standard Co—Cr—Mo alloy (e.g., Co-29Cr-6Mo alloy), by increasing the proportion of the ? phase that is dispersedly precipitated, by sintering an alloy powder produced by gas atomization technique to form pores on the surface of the alloy material, or the like.