Abstract: Disclosed are a laminate film having at least three layers, the three layers being (A) an intermediate layer and (B) two outer layers, the intermediate layer (A) being composed of a resin composition comprising 20 to 100% by weight of an amorphous polyolefin containing at least 50% by weight of a propylene and/or butene-1 and 80 to 0% by weight of a crystalline polypropylene, and the two outer layers (B) being composed of a resin composition comprising a polyolefin and a thermoplastic styrene elastomer, and a laminate film having at least three layers, the three layers being (A) an intermediate layer and (B) two outer layers, the intermediate layer (A) being composed of a resin composition comprising 20 to 100% by weight of an amorphous polyolefin containing at least 50% by weight of a propylene and/or butene-1 and 80 to 0% by weight of a crystalline polypropylene, and the two outer layers (B) being composed of a resin composition comprising a propylene resin and a thermoplastic styrene elastomer.

Abstract: Fibrous magnesium oxysulfate particles having a length of 10 to 100 .mu.m and a thickness of less than 1 .mu.m are used as an antiblocking agent for plastic films, especially polyolefin resin films.

Abstract: A shaped electroconductive thermoplastic resin composition article having a preferable surface appearance is produced by a process including (1) mixing a matrix resinous material containing 100 parts by weight of a thermoplastic resin and, optionally, 120 parts by weight or less of a flame x retardant additive and 40 parts by weight or less of a flame retardant synergistic additive, with 1 to 15% based on the weight of the matrix resinous material, of stainless steel fibers having a length of 2.5 to 7.5 mm and adhered to each other with a thermoplastic resinous adhesive to form a number of bundles; (2) kneading the resultant mixture at an elevated temperature at which the matrix resinous material is melted and (3) shaping the kneaded mixture into a desired form, the kneading the shaping procedures being carried out so that the stainless steel fibers are uniformly dispersed in the melted matrix resinous material and the dispersed stainless steel fibers have an average length of 0.5 to 2.0 mm.

Abstract: Disclosed is a substrate for planographic (lithographic) plate, which comprises metal foils with thicknesses of 5 to 100.mu. laminated onto both surfaces of a sheet which has a thickness of 30 to 400.mu., said sheet being obtained by sheet making of a modified polyolefin composite material comprising 100 parts by weight of a modified polyolefin resin graft-modified partially or wholly with an organic silane compound and 5 to 150 parts by weight of mica.