Abstract: A sliding member having a hard carbon coating that has a thickness of 3 ?m or more and demonstrates high peeling resistance and high wear resistance is provided. A sliding member 100 according to the present disclosure includes a base member 10 and a hard carbon coating 12 that is formed on the base member 10 and has the hydrogen content of 3 atomic % or less and a thickness of 3 ?m or more. When HM represents a Martens hardness of the hard carbon coating 12 and HIT represents an indentation hardness, the ratio HM/HIT is 0.40 or more.

Abstract: A sliding member having a hard carbon coating that has a thickness of 3 ?m or more and demonstrates high peeling resistance and high wear resistance is provided. A sliding member 100 according to the present disclosure includes a base member 10 and a hard carbon coating 12 that is formed on the base member 10 and has the hydrogen content of 3 atomic % or less and a thickness of 3 ?m or more. When HM represents a Martens hardness of the hard carbon coating 12 and HIT represents an indentation hardness, the ratio HM/HIT is 0.40 or more.

Abstract: Provided is a sliding member having a hard carbon coating that makes high wear resistance compatible with a low coefficient of friction and that has excellent peeling resistance. A sliding member (100) includes a base member (10) and a hard carbon coating (12) formed on the base member (10). The indentation hardness of the hard carbon coating (12) decreases gradually from the base member side to the surface side. The hard carbon coating (12) has an indentation hardness distribution at 0?T/Ttotal?0.6 approximated by a first line and an indentation hardness distribution at 0.9?T/Ttotal?1 approximated by a second line, and the intersection between the first line and the second line (T2/Ttotal, H2) satisfies Expression (1), (H3?H1)×T2/Ttotal+H1<H2?0.9×H1, and Expression (2), 0.6?T2/Ttotal?0.9.

Abstract: Provided is a sliding member having a hard carbon coating that makes high wear resistance compatible with a low coefficient of friction and that has excellent peeling resistance. A sliding member (100) includes a base member (10) and a hard carbon coating (12) formed on the base member (10). The indentation hardness of the hard carbon coating (12) decreases gradually from the base member side to the surface side. The hard carbon coating (12) has an indentation hardness distribution at 0?T/Ttotal?0.6 approximated by a first line and an indentation hardness distribution at 0.9?T/Ttotal?1 approximated by a second line, and the intersection between the first line and the second line (T2/Ttotal, H2) satisfies Expression (1), (H3?H1)×T2/Ttotal+H1<H2?0.9×H1, and Expression (2), 0.6?T2/Ttotal?0.9.