Abstract: Disclosed are a resin composition comprising 20 to 50 mass % of a polyphenylene ether-based resin (a), 0.1 to 9 mass % of a polyphenylene ether-based resin modified with an unsaturated carboxylic acid or acid anhydride thereof (b), 15 to 50 mass % of a homopolystyrene (c), 1 to 25 mass % of one or more selected from the group consisting of a hydrogenated block copolymer (d-1) and a rubber-modified polystyrene (d-2), and 5 to 35 mass % of glass fibers (e) which are surface-treated, a resin composition comprising 20 to 50 mass % of a polyphenylene ether-based resin (a), 15 to 50 mass % of a homopolystyrene (c), 5 to 35 mass % of glass fibers (e), and 0.01 to 1 mass % of compounds (f), a method of producing the same, a molded article, and a mechanical component and housing.

Abstract: Provided is a carbon black master batch pellet for black coloring comprising a high concentration of carbon black, having an excellent dispersibility of the carbon black, and which can express a stable black coloring concentration with hardly any classification occurring even when mixed in the various raw materials of a thermoplastic resin composition. A pellet comprising 35 to 55 mass % of carbon black (A), 65 to 45 mass % of a thermoplastic resin (B), and 0 to 10 mass % of a dispersant assistant (C), wherein a diameter (D) in a direction orthogonal to the axial direction is 2 to 5 mm, and a ratio (D/L) of the diameter (D) to a length (L (mm)) in the axial direction is 3.0 to 1.5.

Abstract: Provided is a carbon black master batch pellet for black coloring comprising a high concentration of carbon black, having an excellent dispersibility of the carbon black, and which can express a stable black coloring concentration with hardly any classification occurring even when mixed in the various raw materials of a thermoplastic resin composition. A pellet comprising 35 to 55 mass % of carbon black (A), 65 to 45 mass % of a thermoplastic resin (B), and 0 to 10 mass % of a dispersant assistant (C), wherein a diameter (D) in a direction orthogonal to the axial direction is 2 to 5 mm, and a ratio (D/L) of the diameter (D) to a length (L (mm)) in the axial direction is 3.0 to 1.5.